BiFeO3 thin films with various thicknesses were grown epitaxially on (001) LaSrAlO4 single crystal substrates using pulsed laser deposition. High resolution x-ray diffraction measurements revealed that a tetragonal-like phase with c-lattice constant
~4.65 {AA} is stabilized by a large misfit strain. Besides, a rhombohedral-like phase with c-lattice constant ~3.99 {AA} was also detected at film thickness of ~50 nm and above to relieve large misfit strains. In-plane piezoelectric force microscopy studies showed clear signals and self-assembled nanoscale stripe domain structure for the tetragonal-like regions. These findings suggest a complex picture of nanoscale domain patterns in BiFeO3 thin films subjected to large compressive strains.
A morphotropic phase boundary driven by epitaxial strain has been observed in a lead-free multiferroic BiFeO3 thin films and the strain-driven phase transitions were widely reported to be iso-symmetric Cc-Cc ones by recent works. In this paper, we su
ggest that the tetragonal-like BiFeO3 phase identified in epitaxial films on (001) LaAlO3 single crystal substrates is monoclinic MC. This MC phase is different from MA type monoclinic phase reported in BiFeO3 films grown on low mismatch substrates, such as SrTiO3. This is confirmed not only by synchrotron x-ray studies but also by piezoresponse force microscopy measurements. The polarization vectors of the tetragonal-like phase lie in the (100) plane, not the (110) plane as previously reported. A phenomenological analysis was proposed to explain the formation of MC Phase. Such a low symmetry MC phase, with its linkage to MA phase and the multiphase coexistence open an avenue for large piezoelectric response in BiFeO3 films and shed light on a complete understanding towards possible polarization rotation paths and enhanced multiferroicity in BiFeO3 films mediated by epitaxial strain. This work may also aid the understanding of developing new lead-free strain-driven morphotropic phase boundary in other ferroic systems.