La0.7Sr0.3MnO3 (LSMO) films with extraordinarily wide atomic terraces are epitaxially grown on SrTiO3 (100) substrates by pulsed laser deposition. Atomic force microscopy measurements on the LSMO films show that the atomic step is ~ 4 {AA} and the at
omic terrace width is more than 2 micrometers. For a 20 monolayers (MLs) LSMO film, the magnetization is determined to be 255 +- 15 emu/cm3 at room temperature, corresponding to 1.70 + - 0.11 Bohr magneton per Mn atom. As the thickness of LSMO increases from 8 MLs to 20 MLs, the critical thickness for the temperature dependent insulator-to-metal behavior transition is shown to be 9 MLs. Furthermore, post-annealing in oxygen environment improves the electron transport and magnetic properties of the LSMO films.
As a non-magnetic heavy metal is attached to a ferromagnet, a vertically flowing heat-driven spin current is converted to a transverse electric voltage, which is known as the longitudinal spin Seebeck effect (SSE). If the ferromagnet is a metal, this
voltage is also accompanied by voltages from two other sources, i.e. the anomalous Nernst effect in both the ferromagnet and the proximity-induced ferromagnetic boundary layer. By properly identifying and carefully separating those different effects, we find that in this pure spin current circuit the additional spin current drawn by the heavy metal generates another significant voltage by the ferromagnetic metal itself which should be present in all relevant experiments.