We investigated the electronic properties of epitaxially stabilized perovskite SrIrO3 and demonstrated the effective strain-control on its electronic structure. Comprehensive transport measurements showed that the strong spin-orbit coupling renders a
novel semimetallic phase for the J_eff=1/2 electrons rather than an ordinary correlated metal, elucidating the nontrivial mechanism underlying the dimensionality-controlled metal-insulator transition in iridates. The electron-hole symmetry of this correlated semimetal was found to exhibit drastic variation when subject to bi-axial strain. Under compressive strain, substantial electron-hole asymmetry is observed in contrast to the tensile side, where the electron and hole effective masses are comparable, illustrating the susceptivity of the J_eff=1/2 to structural distortion. Tensile strain also shrinks the Fermi surface, indicative of an increasing degree of correlation which is consistent with optical measurements. These results pave a pathway to investigate and manipulate the electronic states in spin-orbit-coupled correlated oxides, and lay the foundation for constructing 5d transition metal heterostructures.
High quality epitaxial thin films of Jeff=1/2 Mott insulator Sr2IrO4 with increasing in-plane tensile strain have been grown on top of SrTiO3(001) substrates. Increasing the in-plane tensile strain up to ~0.3% was observed to drop the c/a tetragonali
ty by 1.2 %. X-ray absorption spectroscopy detected a strong reduction of the linear dichroism upon increasing in-plane tensile strain towards a reduced anisotropy in the local electronic structure. While the most relaxed thin film shows a consistent dependence with previously reported single crystal bulk measurements, electrical transport reveals a charge gap reduction from 200 meV down to 50 meV for the thinnest and most epitaxy-distorted film. We argue that the reduced tetragonality plays a major role in the change of the electronic structure, which is reflected in the change of the transport properties. Our work opens the possibility for exploiting epitaxial strain as a tool for both structural and functional manipulation of spin-orbit Mott systems.