We present a comprehensive study of polar and magnetic excitations in BiFeO3 ceramics and a thin film epitaxially grown on an orthorhombic (110) TbScO3 substrate. Infrared reflectivity spectroscopy was performed at temperatures from 5 to 900 K for th
e ceramics and below room temperature for the thin film. All 13 polar phonons allowed by the factor-group analysis were observed in theceramic samples. The thin-film spectra revealed 12 phonon modes only and an additional weak excitation, probably of spin origin. On heating towards the ferroelectric phase transition near 1100 K, some phonons soften, leading to an increase in the static permittivity. In the ceramics, terahertz transmission spectra show five low-energy magnetic excitations including two which were not previously known to be infrared active; at 5 K, their frequencies are 53 and 56 cm-1. Heating induces softening of all magnetic modes. At a temperature of 5 K, applying an external magnetic field of up to 7 T irreversibly alters the intensities of some of these modes. The frequencies of the observed spin excitations provide support for the recently developed complex model of magnetic interactions in BiFeO3 (R.S. Fishman, Phys. Rev. B 87, 224419 (2013)). The simultaneous infrared and Raman activity of the spin excitations is consistent with their assignment to electromagnons.
We report an investigation of hexagonal Y_(1-x)Eu_xMnO_3 ceramics with x=0, 0.1 and 0.2 using infrared and THz spectroscopies in the temperature range between 5 and 900 K. The temperature dependence of the THz permittivity reveals a kink near the ant
iferromagnetic phase transition temperature T_N ~ 70 K giving evidence of a strong spin-lattice coupling. Below T_N two absorption peaks were revealed in the THz spectra close to 43 and 73 cm-1. While the first peak corresponds to a sharp antiferromagnetic resonance exhibiting softening on heating towards TN, the second one may be attributed to an impurity mode or a multiphonon absorption peak. High-temperature THz spectra measured up to 900 K reveal only small gradual increase of the permittivity in agreement with a weak phonon softening observed in the infrared reflectance spectra upon heating. This corresponds to an improper ferroelectric character of the phase transition proposed from first principle calculations by Fennie and Rabe [Phys. Rev. B 72 (2005), pp. 100103(R)].