We investigate the structural and optical properties of spontaneously formed GaN nanowires with different degrees of coalescence. This quantity is determined by an analysis of the cross-sectional area and perimeter of the nanowires obtained by plan-v
iew scanning electron microscopy. X-ray diffraction experiments are used to measure the inhomogeneous strain in the nanowire ensembles as well as the orientational distribution of the nanowires. The comparison of the results obtained for GaN nanowire ensembles prepared on bare Si(111) and AlN buffered 6H-SiC(000-1) reveals that the main source of the inhomogeneous strain is the random distortions caused by the coalescence of adjacent nanowires. The magnitude of the strain inhomogeneity induced by nanowire coalescence is found not to be determined solely by the coalescence degree, but also by the mutual misorientation of the coalesced nanowires. The linewidth of the donor-bound exciton transition in photoluminescence spectra does not exhibit a monotonic increase with the coalescence degree. In contrast, the comparison of the root mean square strain with the linewidth of the donor-bound exciton transition reveals a clear correlation: the higher the strain inhomogeneity, the larger the linewidth.
We investigate the nature of excitons bound to I1 basal-plane stacking faults [(I1;X)] in GaN nanowire ensembles by continuous-wave and time-resolved photoluminescence spectroscopy. Based on the linear increase of the radiative lifetime of these exci
tons with temperature, they are demonstrated to exhibit a two-dimensional density of states, i. e., a basal-plane stacking fault acts as a quantum well. From the slope of the linear increase, we determine the oscillator strength of the (I1;X) and show that the value obtained reflects the presence of large internal electrostatic fields across the stacking fault. While the recombination of donor-bound and free excitons in the GaN nanowire ensemble is dominated by nonradiative phenonema already at 10 K, we observe that the (I1;X) recombines purely radiatively up to 60 K. This finding provides important insight into the nonradiative recombination processes in GaN nanowires. First, the radiative lifetime of about 6 ns measured at 60 K sets an upper limit for the surface recombination velocity of 450 cm/s considering the nanowires mean diameter of 105 nm. Second, the density of nonradiative centers responsible for the fast decay of donor-bound and free excitons cannot be higher than 2x10^16 cm^-3. As a consequence, the nonradiative decay of donor-bound excitons in these GaN nanowire ensembles has to occur indirectly via the free exciton state.