A novel method to prepare bulk Fe(Se0.5Te0.5) samples is presented, based on a melting process and a subsequent annealing treatment. With respect to the standard sintering technique, it produces much more homogeneous and denser samples, characterized
by large and well interconnected grains. The resulting samples exhibit optimal critical temperature values, sharp resistive and magnetic transitions, large magnetic hysteresis loops and high upper critical fields are observed. Interestingly, the global critical current density is much enhanced as compared to the values reported in literature for bulk samples of the same 11 family, reaching about 103 A/cm2 at zero field at 4.2 K as assessed by magnetic, transport and magneto-optical techniques. Even more importantly, its field dependence turns out to be very weak, such that at mu_{0}H = 7 T it is suppressed only by a factor sim2.
The MgB2 superconductor has already demonstrated its applicative potential, in particular for DC applications such as MRI magnets, thanks to the low costs of the raw materials and to its simple production process. However further efforts have still t
o be made in order to broaden its employment also towards the AC applications such as SFCL, motors, transformers. The main issues are related to the reduction of the AC losses. Some of these can be faced by obtaining multifilamentary conductors with a large number of very fine filaments and, in this context, the powders granulometry can play a crucial role. We have prepared MgB2 starting powders with different granulometries and by the ex-situ P.I.T method we have realized multifilamentary wires with a number of filaments up to 361 and an average size of each filament lowered down to 30 microns. In particular we have studied the relationship between grain and filament size in terms of transport properties and show that the optimization of this ratio is possible in order to obtain suitable conductors for AC industrial applications.