When magnetic nanoparticles (MNPs) are single-domain and magnetically independent, their magnetic properties and the conditions to optimize their efficiency in magnetic hyperthermia applications are now well-understood. However, the influence of magn
etic interactions on magnetic hyperthermia properties is still unclear. Here, we report hyperthermia and high-frequency hysteresis loop measurements on a model system consisting of MNPs with the same size but a varying anisotropy, which is an interesting way to tune the relative strength of magnetic interactions. A clear correlation between the MNP anisotropy and the squareness of their hysteresis loop in colloidal solution is observed : the larger the anisotropy, the smaller the squareness. Since low anisotropy MNPs display a squareness higher than the one of magnetically independent nanoparticles, magnetic interactions enhance their heating power in this case. Hysteresis loop calculations of independent and coupled MNPs are compared to experimental results. It is shown that the observed features are a natural consequence of the formation of chains and columns of MNPs during hyperthermia experiments: in these structures, when the MNP magnetocristalline anisotropy is small enough to be dominated by magnetic interactions, the hysteresis loop shape tends to be rectangular, which enhance their efficiency. On the contrary, when MNPs do not form chains and columns, magnetic interactions reduces the hysteresis loop squareness and the efficiency of MNPs compared to independent ones. The present work should improve the understanding and interpretation of magnetic hyperthermia experiments.
We report on the magnetic and hyperthermia properties of iron nanoparticles synthesized by organometallic chemistry. They are 5.5 nm in diameter and display a saturation magnetization close to the bulk one. Magnetic properties are dominated by the co
ntribution of aggregates of nanoparticles with respect to individual isolated nanoparticles. Alternative susceptibility measurements are been performed on a low interacting system obtained after eliminating the aggregates by centrifugation. A quantitative analysis using the Gittleman s model allow a determination of the effective anisotropy Keff = 1.3 * 10^5 J.m^{-3}, more than two times the magnetocristalline value of bulk iron. Hyperthermia measurements are performed on agglomerates of nanoparticles at a magnetic field up to 66 mT and at frequencies in the range 5-300 kHz. Maximum measured SAR is 280 W/g at 300 kHz and 66 mT. Specific absorption rate (SAR) displays a square dependence with the magnetic field below 30 mT but deviates from this power law at higher value. SAR is linear with the applied frequency for mu_0H=19 mT. The deviations from the linear response theory are discussed. A refined estimation of the optimal size of iron nanoparticles for hyperthermia applications is provided using the determined effective anisotropy value.
We report on the magnetic hyperthermia properties of chemically synthesized ferromagnetic 11 and 16 nm Fe(0) nanoparticles of cubic shape displaying the saturation magnetization of bulk iron. The specific absorption rate measured on 16 nm nanocubes i
s 1690+-160 W/g at 300 kHz and 66 mT. This corresponds to specific losses-per-cycle of 5.6 mJ/g, largely exceeding the ones reported in other systems. A way to quantify the degree of optimization of any system with respect to hyperthermia applications is proposed. Applied here, this method shows that our nanoparticles are not fully optimized, probably due to the strong influence of magnetic interactions on their magnetic response. Once protected from oxidation and further optimized, such nano-objects could constitute efficient magnetic cores for biomedical applications requiring very large heating power.