We report on a systematic study of the structural, magnetic and transport properties of high-purity 1T-VS$_2$ powder samples prepared under high pressure. The results differ notably from those previously obtained by de-intercalating Li from LiVS$_2$.
First, no Charge Density Wave (CDW) is found by transmission electron microscopy down to 94 K. Though, textit{ab initio} phonon calculations unveil a latent CDW instability driven by an acoustic phonon softening at the wave vector ${bf q}_{CDW} approx$ (0.21,0.21,0) previously reported in de-intercalated samples. A further indication of latent lattice instability is given by an anomalous expansion of the V-S bond distance at low temperature. Second, infrared optical absorption and electrical resistivity measurements give evidence of non metallic properties, consistent with the observation of no CDW phase. On the other hand, magnetic susceptibility and NMR data suggest the coexistence of localized moments with metallic carriers, in agreement with textit{ab initio} band structure calculations. This discrepancy is reconciled by a picture of electron localization induced by disorder or electronic correlations leading to a phase separation of metallic and non-metallic domains in the nm scale. We conclude that 1T-VS$_2$ is at the verge of a CDW transition and suggest that residual electronic doping in Li de-intercalated samples stabilizes a uniform CDW phase with metallic properties.
By means of neutron powder diffraction, we investigated the effect of the polar Bi$^{3+}$ ion on the magnetic ordering of the Mn$^{3+}$ ions in BiMn$_3$Mn$_4$O$_{12}$, the counterpart with textit{quadruple} perovskite structure of the textit{simple}
perovskite BiMnO$_3$. The data are consistent with a textit{noncentrosymmetric} spacegroup $Im$ which contrasts the textit{centrosymmetric} one $I2/m$ previously reported for the isovalent and isomorphic compound LaMn$_3$Mn$_4$O$_{12}$, which gives evidence of a Bi$^{3+}$-induced polarization of the lattice. At low temperature, the two Mn$^{3+}$ sublattices of the $A$ and $B$ sites order antiferromagnetically (AFM) in an independent manner at 25 and 55 K, similarly to the case of LaMn$_3$Mn$_4$O$_{12}$. However, both magnetic structures of BiMn$_3$Mn$_4$O$_{12}$ radically differ from those of LaMn$_3$Mn$_4$O$_{12}$. In BiMn$_3$Mn$_4$O$_{12}$ the moments $textbf{M}_{A}$ of the $A$ sites form an anti-body AFM structure, whilst the moments textbf{M}$_{B}$ of the $B$ sites result from a large and textit{uniform} modulation $pm textbf{M}_{B,b}$ along the b-axis of the moments textbf{M}$_{B,ac}$ in the $ac$-plane. The modulation is strikingly correlated with the displacements of the Mn$^{3+}$ ions induced by the Bi$^{3+}$ ions. Our analysis unveils a strong magnetoelastic coupling between the internal strain created by the Bi$^{3+}$ ions and the moment of the Mn$^{3+}$ ions in the $B$ sites. This is ascribed to the high symmetry of the oxygen sites and to the absence of oxygen defects, two characteristics of quadruple perovskites not found in simple ones, which prevent the release of the Bi$^{3+}$-induced strain through distortions or disorder. This demonstrates the possibility of a large magnetoelectric coupling in proper ferroelectrics and suggests a novel concept of internal strain engineering for multiferroics design.
By means of synchrotron X-ray diffraction, we studied the effect of high pressure, P, up to 13 GPa on the room temperature crystal structure of superconducting CaC6. In this P range, no change of the pristine space group symmetry, textit{R=3m}, is fo
und. However, at 9 GPa, i.e. close to the critical value at which a large T_c reduction was reported recently, we observed a compressibility jump concomitant to a large broadening of Bragg peaks. The reversibility of both effects upon depressurization and symmetry arguments give evidence of an order-disorder phase transition of second order, presumably associated with the Ca sublattice, which provides a full account for the above Tc reduction.