Hot wall technique was used to grow block single crystal films of Bi_2Te_3 and solid solutions of Bi_(0.5)Sb_(1.5)Te_3 on mica (muscovite) substrates. X-ray diffraction studies demonstrated that the crystalline c-axis in the films was normal to the substrate plane. Seebeck coefficient, electrical conductivity and magnetoresistivity tensor components were measured at various orientations of magnetic and electric fields in the temperature interval 77-300 K and magnetic field up to 14 T. Scattering mechanism of charge carriers in the films were studied using temperature dependences of the degeneracy parameter and the Seebeck coefficient in terms of a many-valley model of energy spectrum. Obtained results have shown that the effective scattering parameter is considerably differed from the value specific for an acoustic scattering of charge carriers in the weakly degenerate films due to an additional scattering of charge carriers on interface and interctystallite boundaries. These features of charge carrier scattering are supposed to affect electronic transport in the films and enhance figure of merit.
rate research
Read More
Chalcogenide perovskites have emerged as a new class of electronic materials, but fundamental properties and applications of chalcogenide perovskites remain limited by the lack of high quality epitaxial thin films. We report epitaxial thin film growth of BaZrS3, a prototypical chalcogenide, by pulsed laser deposition. X-ray diffraction studies show that the films are strongly textured out of plane and have a clear in-plane epitaxial relationship with the substrate. Electron microscopy studies confirm the presence of epitaxy for the first few layers of the film at the interface, even though away from the interface the films are polycrystalline with a large number of extended defects suggesting the potential for further improvement in growth. X-Ray reflectivity and atomic force microscopy show smooth film surfaces and interfaces between the substrate and the film. The films show strong light absorption near the band edge and photoluminescence in the visible region. The photodetector devices show fast and efficient photo response with the highest ON/OFF ratio reported for BaZrS3 films thus far. Our study opens up opportunities to realize epitaxial thin films, heterostructures, and superlattices of chalcogenide perovskites to probe fundamental physical phenomena and the resultant electronic and photonic device technologies.
The layered Bi-chalcogenide compounds have been drawing much attention as a new layered superconductor family since 2012. Due to the rich variation of crystal structure and constituent elements, the development of new physics and chemistry of the layered Bi-chalcogenide family and its applications as functional materials have been expected. Recently, it was revealed that the layered Bi chalcogenides can show a relatively high thermoelectric performance (ZT = 0.36 in LaOBiSSe at ~650 K). Here, we show the crystal structure variation of the Bi-chalcogenide family and their thermoelectric properties. Finally, the possible strategies for enhancing the thermoelectric performance are discussed on the basis of the experimental and the theoretical facts reviewed here.
SrTiO$_3$ is a promising $n$-type oxide semiconductor for thermoelectric energy conversion. Epitaxial thin films of SrTiO$_3$ doped with both La and oxygen vacancies have been synthesized by pulsed laser deposition (PLD). The thermoelectric and galvanomagnetic properties of these films have been characterized at temperatures ranging from 300 K to 900 K and are typical of a doped semiconductor. Thermopower values of double-doped films are comparable to previous studies of La doped single crystals at similar carrier concentrations. The highest thermoelectric figure of merit ($ZT$) was measured to be 0.28 at 873 K at a carrier concentration of $2.5times10^{21}$ cm$^{-3}$.
The double perovskite Sr2CrReO6 is an interesting material for spintronics, showing ferrimagnetism up to 635 K with a predicted high spin polarization of about 86%. We fabricated Sr2CrReO6 epitaxial films by pulsed laser deposition on (001)-oriented SrTiO3 substrates. Phase-pure films with optimum crystallographic and magnetic properties were obtained by growing at a substrate temperature of 700 degree C in pure O2 of 6.6x10-4 mbar. The films are c-axis oriented, coherently strained, and show less than 20% anti-site defects. The magnetization curves reveal high saturation magnetization of 0.8 muB per formula unit and high coercivity of 1.1 T, as well as a strong magnetic anisotropy.
CaFe2O4 is a highly anisotropic antiferromagnet reported to display two spin arrangements with up-up-down-down (phase A) and up-down-up-down (phase B) configurations. The relative stability of these phases is ruled by the competing ferromagnetic and antiferromagnetic interactions between Fe3+ spins arranged in two different environments, but a complete understanding of the magnetic structure of this material does not exist yet. In this study we investigate epitaxial CaFe2O4 thin films grown on TiO2 (110) substrates by means of Pulsed Laser Deposition (PLD). Structural characterization reveals the coexistence of two out-of-plane crystal orientations and the formation of three in-plane oriented domains. The magnetic properties of the films, investigated macroscopically as well as locally, including highly sensitive Mossbauer spectroscopy, reveal the presence of just one order parameter showing long-range ordering below T = 185 K and the critical nature of the transition. In addition, a non-zero in-plane magnetization is found, consistent with the presence of uncompensated spins at phase or domain boundaries, as proposed for bulk samples.
Log in to be able to interact and post comments
comments
Fetching comments
Sign in to be able to follow your search criteria