Defined substoichiometric titanium oxides (Ti$_x$O$_{2x-1}$ with $3 < x < 10$) called Magneli phases have been investigated mostly for their unusual high conductivity and metal-like behavior. In photocatalysis, Magneli phase containing titania particles have been reported to provide favorable charge separation resulting in enhanced reaction efficiency. In the current work we describe a one-step synthesis of Magneli-containing mixed phase nanoparticles that carry directly integrated minute amounts of Pt. Phase optimized nanoparticles that contain only a few hundred ppm Pt are very effective photocatalysts for H$_2$ evolution (they provide a 50-100 times higher H$_2$ evolution than plain anatase loaded with a similar amount of Pt). These photocatalysts are synthesized in a setup combining a hot-wall reactor that is used for TiOx synthesis with a spark generator producing Pt nanoparticles. Different reactor temperatures result in various phase ratios between anatase and Magneli phases. The titania nanoparticles (ca. 24 - 53 nm) were characterized using XRD, HRTEM, XPS and EPR spectra as well as ICP-OES analysis. The best photocatalyst prepared at 900$^circ$C (which consists of mixed phase particles of 32% anatase, 11% rutile and 57% Magneli phases loaded with 290 ppm of Pt) can provide a photocatalytic H$_2$ evolution rate of ca. 5432 micromol h$^{-1} g$^{-1}$ for UV and ca. 1670 micromol h$^{-1} g$^{-1}$ for AM1.5 illumination. For powders converted to higher amounts of Magneli phases (1000$^circ$C and 1100$^circ$C), a drastic loss of the photocatalytic H$_2$ generation activity is observed. Thus, the high photocatalytic efficiency under best conditions is ascribed to an effective synergy between multi-junctions of Magneli titania and Pt that enable a much more effective charge separation and reaction than conventional Pt/anatase junctions.
rate research
Read More
Magneli phases of titanium dioxide (such as Ti4O7, Ti5O9, etc.) provide electronic properties, namely a stable metallic behavior at room temperature. In this manuscript, we demonstrate that nanoscopic Magneli phases, formed intrinsically in anatase during a thermal aerosol synthesis, can enable significant photocatalytic H2 generation. This without the use of any extrinsic co-catalyst in anatase. Under optimized conditions, mixed phase particles of 30 percent anatase, 25 percent Ti4O7 and 20 percent Ti5O9 are obtained that can provide, under solar light, direct photocatalytic H2 evolution at a rate of 145 micromol h-1 g-1. These anatase particles contain 5-10 nm size inter-grown phases of Ti4O7 and Ti5O9. Key is the metallic band of Ti4O7 that induces a particle internal charge separation and transfer cascade with suitable energetics and favorable dimensions that are highly effective for H2 generation.
In this work, we demonstrate that a well-established and facile ball milling approach using mixtures of commercial anatase nanoparticles and TiH2 introduces noble-metal-free photocatalytic H2 activity to titania. We characterize this synergistic effect in view of the nature of defects, state of hydroxylation, and investigate the effect on the energetics and kinetics of electronic states and the resulting H2 evolution performance.
The design of efficient electrocatalysts for electrochemical water splitting with minimal amount of precious metal is crucial to attain renewable and sustainable energy conversion. Here, we report the use of a network of CdSe branched colloidal nanocrystals, made of a CdSe core and eight CdSe pods (so-called octapods), able to host on their pods Pt particles, and thus catalyzing water splitting reactions. Thanks to the octapod shape, the resulting Pt-hosting network is mechanically trapped onto carbon nanotube buckypaper, providing mechanically flexible and binder-free electrodes. We found that such hierarchical configuration maximizes the mass activity and the utilization efficiency of Pt for the hydrogen evolution reaction (HER). At a potential of -0.15 V vs. reversible hydrogen electrode, the Pt/octapod network-based electrodes display a Pt mass activity on the HER of 166 A mg-1 and 42 A mg-1 in acidic and alkaline media, respectively. These values correspond to turnover frequencies of 168 s-1 and 42 s-1, respectively, which are in that order 14 and 21 times higher compared to commercially available Pt/C benchmarks. The strong chemical and mechanical interactions between the Pt and the octapod surface, along with pod-aided adhesion of the Pt/octapod network to the buckypaper, result in a long-term durability (>20 h) of the HER-activity in both media. These results experimentally prove that the exploitation of our network of branched nanocrystals hosting Pt particles can circumvent the durability issues of the catalysts while adopting either ultralow Pt loadings or benchmarking carbon-supported Pt nanocrystals. Our work opens up prospects for using porous networks made by branched nanocrystals as catalysts with ultralow amount of noble metals and controlled catalytic properties.
The low energy electronic structure of LaFeAsO1-xHx (0.0 < x < 0.60), the system which exhibits two superconducting domes in its phase diagram, is investigated by utilizing the laser photoemission spectroscopy. From the precise temperature-dependent measurement of the spectra near the Fermi level, we find the suppression of the density of states with cooling, namely the pseudogap formation, for all doping range. The pseudogap in the low x range (i.e. the first superconducting dome regime) gets suppressed with increasing x, more or less similarly to the previous results in F-doped LaFeAsO system. On the other hand, the pseudogap behavior in the second superconducting dome regime at high-x becomes stronger with increasing the H-doping level. The systematic doping dependence shows that the pseudogap is enhanced toward the both ends of the phase diagram where the different types of antiferromagnetic order exist.
The high-throughput scalable production of cheap, efficient and durable electrocatalysts that work well at high current densities demanded by industry is a great challenge for the large-scale implementation of electrochemical technologies. Here we report the production of a 2D MoS2-based ink-type electrocatalyst by a scalable top-down exfoliation technique followed by a simple heat treatment. The catalyst shows a high current density of 1000 mA cm^-2 at an overpotential of 454 mV for the hydrogen evolution reaction (HER) without the need of iR correction, as well as good stability over 24 hours. Using the same method, we have, for the first time, produced a cheap MoS2 mineral-based catalyst and found that it had an excellent performance for high-current-density HER. Noteworthy, production rate of this MoS2-based catalyst is one to two orders of magnitude higher than those previously reported. In addition, the price of the MoS2 mineral is five orders of magnitude lower than commercial Pt catalysts, making the MoS2 mineral-based catalyst cheap, and the ink-type catalyst dispersions can be easily integrated with other technologies for large-scale catalyst electrode preparation. These advantages indicate the huge potentials of this method and mineral-based cheap and abundant natural resources as catalysts in the electrochemical technologies.