Hydrogen adsorption on graphene can be increased by functionalization with Ti. This requires dispersing Ti islands on graphene as small and dense as possible, in order to increase the number of hydrogen adsorption sites per Ti atom. In this report, we investigate the morphology of Ti on nanocrystalline graphene and its hydrogen adsorption by scanning tunneling microscopy and thermal desorption spectroscopy, and compare the results with equivalent measurements on single-crystalline graphene. Nanocrystalline graphene consists of extremely small crystal grains of < 5 nm size. Ti atoms preferentially adsorb at the grain boundaries of nanocrystalline graphene and form smaller and denser islands compared to single-crystalline graphene. Surprisingly, however, hydrogen adsorbs less to Ti on nanocrystalline graphene than to Ti on single-crystalline graphene. In particular, hydrogen hardly chemisorbs to 1 ML of Ti on nanocrystalline graphene. This may be attributed to strong bonds between Ti and defects located along the grain boundaries in nanocrystalline graphene. This mechanism might apply to other metals, as well, and therefore our results suggest that when functionalizing graphene by metal atoms for the purpose of hydrogen storage or other chemical reactions, it is important to consider not only the morphology of the resulting surface, but also the influence of graphene on the electronic states of the metal.
rate research
Read More
The effect of oxygen adsorption on the local structure and electronic properties of monolayer graphene grown on SiC(0001) has been studied by means of Low Energy Electron Microscopy (LEEM), microprobe Low Energy Electron Diffraction (muLEED) and microprobe Angle Resolved Photoemission (muARPES). We show that the buffer layer of epitaxial graphene on SiC(0001) is partially decoupled after oxidation. The monitoring of the oxidation process demonstrates that the oxygen saturates the Si dangling bonds, breaks some Si-C bonds at the interface and intercalates the graphene layer. Accurate control over the oxidation parameters enables us to tune the charge density modulation in the layer.
We report our results on the adsorption of noble gases such as argon, krypton and xenon on a graphene sheet, using Grand Canonical Monte Carlo (GCMC) simulations. We calculated the two-dimensional gas-liquid critical temperature for each adsorbate, resulting in fair agreement with theoretical predictions and experimental values of gases on graphite. We determined the different phases of the monolayers and constructed the phase diagrams. We found two-dimensional incommensurate solid phases for krypton, argon and xenon, and a two-dimensional commensurate solid phase for krypton.
The ability of atomic hydrogen to chemisorb on graphene makes the latter a promising material for hydrogen storage. Based on scanning tunneling microscopy techniques, we report on site-selective adsorption of atomic hydrogen on convexly curved regions of monolayer graphene grown on SiC(0001). This system exhibits an intrinsic curvature owing to the interaction with the substrate. We show that at low coverage hydrogen is found on convex areas of the graphene lattice. No hydrogen is detected on concave regions. These findings are in agreement with theoretical models which suggest that both binding energy and adsorption barrier can be tuned by controlling the local curvature of the graphene lattice. This curvature-dependence combined with the known graphene flexibility may be exploited for storage and controlled release of hydrogen at room temperature making it a valuable candidate for the implementation of hydrogen-storage devices.
The adsorption structure of the molecular switch azobenzene on Ag(111) is investigated by a combination of normal incidence x-ray standing waves and dispersion-corrected density functional theory. The inclusion of non-local collective substrate response (screening) in the dispersion correction improves the description of dense monolayers of azobenzene, which exhibit a substantial torsion of the molecule. Nevertheless, for a quantitative agreement with experiment explicit consideration of the effect of vibrational mode anharmonicity on the adsorption geometry is crucial.
Investigation of phosphate species adsorption/desorption processes was performed on Ag(100) and Ag(111) electrodes in H$_{3}$PO$_{4}$, KH$_{2}$PO$_{4}$ and K$_{3}$PO$_{4}$ solutions by Current-Potential ($j-V$) profiles and Electrochemical Impedance Spectroscopy ($EIS$). We used the equivalent circuit method to fit the impedance spectra. Different electrical equivalent circuits ($EECs$) were employed depending on the potential region that was analyzed. For potentials more negative than the onset of the hydrogen evolution reaction ($her$), a charge transfer resistance (R$_{ct}$) in parallel to the $(RC)$ branches was included. Peaks from $j-V$ profiles were integrated to estimate surface coverage. A reversible process was observed for Ag(hkl)/KH$_{2}$PO$_{4}$ systems, where a value of 0.07 ML was obtained. For Ag(111)/H$_{3}$PO$_{4}$, a coverage of about 0.024 ML was calculated from anodic/cathodic $j-V$ profiles, whereas for Ag(hkl)/K$_{3}$PO$_{4}$ systems different values were obtained from integration of anodic/cathodic peaks due to highly irreversible processes were observed. In the case of Ag(hkl)/K$_{3}$PO$_{4}$, the capacitance (C$_{(phi)}$) plots are well differentiated for the two faces, and co-adsorption of OH$^{-}$ was evaluated from resistance parameters. Characteristic face-specific relaxation times are obtained for each electrode. In addition, it was found that the onset potential of $her$ for Ag(111) at pH=1.60 was about 100 mV more negative compare to Ag(100).