Register a new userOrigin of the Large Perpendicular Magnetic Anisotropy in Nanometer-thick Epitaxial Graphene/Co/Heavy Metal Heterostructures
133
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
A combination of theoretical modelling and experiments reveals the origin of the large perpendicular magnetic anisotropy (PMA) that appears in nanometer-thick epitaxial Co films intercalated between graphene (Gr) and a heavy metal (HM) substrate, as a function of the Co thickness. High quality epitaxial Gr/Co /HM(111) (HM=Pt,Ir) heterostructures are grown by intercalation below graphene, which acts as a surfactant that kinetically stabilizes the pseudomorphic growth of highly perfect Co face-centered tetragonal ($fct$) films, with a reduced number of stacking faults as the only structural defect observable by high resolution scanning transmission electron microscopy (HR-STEM). Magneto-optic Kerr effect (MOKE) measurements show that such heterostructures present PMA up to large Co critical thicknesses of about 4~nm (20~ML) and 2~nm (10~ML) for Pt and Ir substrates, respectively, while X-ray magnetic circular dichroism (XMCD) measurements show an inverse power law of the anistropy of the orbital moment with Co thickness, reflecting its interfacial nature, that changes sign at about the same critical values. First principles calculations show that, regardless of the presence of graphene, ideal Co $fct$ films on HM buffers do not sustain PMAs beyond around 6~MLs due to the in-plane contribution of the inner bulk-like Co layers. The large experimental critical thicknesses sustaining PMA can only be retrieved by the inclusion of structural defects that promote a local $hcp$ stacking such as twin boundaries or stacking faults. Remarkably, a layer resolved analysis of the orbital momentum anisotropy reproduces its interfacial nature, and reveals that the Gr/Co interface contribution is comparable to that of the Co/Pt(Ir).
rate research
Read More
We investigated perpendicular magnetic anisotropy (PMA) and related properties of epitaxial Fe (0.7 nm)/MgAl2O4(001) heterostructures prepared by electron-beam evaporation. Using an optimized structure, we obtained a large PMA energy ~1 MJ/m3 at room temperature, comparable to that in ultrathin-Fe/MgO(001) heterostructures. Both the PMA energy and saturation magnetization show weak temperature dependence, ensuring wide working temperature in application. The effective magnetic damping constant of the 0.7 nm Fe layer was ~0.02 using time-resolved magneto-optical Kerr effect. This study demonstrates capability of the Fe/MgAl2O4 heterostructure for perpendicular magnetic tunnel junctions, as well as a good agreement with theoretical predictions.
We have studied the magnetic properties of multilayers composed of ferromagnetic metal Co and heavy metals with strong spin orbit coupling (Pt and Ir). Multilayers with symmetric (ABA stacking) and asymmetric (ABC stacking) structures are grown to study the effect of broken structural inversion symmetry. We compare the perpendicular magnetic anisotropy (PMA) energy of symmetric Pt/Co/Pt, Ir/Co/Ir multilayers and asymmetric Pt/Co/Ir, Ir/Co/Pt multilayers. First, the interface contribution to the PMA is studied using the Co layer thickness dependence of the effective PMA energy. Comparison of the interfacial PMA between the Ir/Co/Pt, Pt/Co/Ir asymmetric structures and Pt/Co/Pt, Ir/Co/Ir symmetric structures indicate that the broken structural inversion symmetry induced PMA is small compared to the overall interfacial PMA. Second, we find the magnetic anisotropy field is significantly increased in multilayers when the ferromagnetic layers are antiferromagnetically coupled via interlayer exchange coupling (IEC). Macrospin model calculations can qualitatively account for the relation between the anisotropy field and the IEC. Among the structures studied, IEC is the largest for the asymmetric Ir/Co/Pt multilayers: the exchange coupling field exceeds 3 T and consequently, the anisotropy field approaches 10 T. Third, comparing the asymmetric Ir/Co/Pt and Pt/Co/Ir structures, we find the IEC and, to some extent, the interface PMA are stronger for the former than the latter. X-ray magnetic circular dichroism studies suggest that the proximity induced magnetization in Pt is larger for the Ir/Co/Pt multilayers than the inverted structure, which may partly account for the difference in the magnetic properties. These results show the intricate relation between PMA, IEC and the proximity induced magnetization that can be exploited to design artificial structures with unique magnetic characteristics.
Spin waves in ferrimagnetic yttrium iron garnet (YIG) films with ultralow magnetic damping are relevant for magnon-based spintronics and low-power wave-like computing. The excitation frequency of spin waves in YIG is rather low in weak external magnetic fields because of its small saturation magnetization, which limits the potential of YIG films for high-frequency applications. Here, we demonstrate how exchange-coupling to a CoFeB film enables efficient excitation of high-frequency perpendicular standing spin waves (PSSWs) in nanometer-thick (80 nm and 295 nm) YIG films using uniform microwave magnetic fields. In the 295-nm-thick YIG film, we measure intense PSSW modes up to 10th order. Strong hybridization between the PSSW modes and the ferromagnetic resonance mode of CoFeB leads to characteristic anti-crossing behavior in broadband spin-wave spectra. A dynamic exchange torque at the YIG/CoFeB interface explains the excitation of PSSWs. The localized torque originates from exchange coupling between two dissimilar magnetization precessions in the YIG and CoFeB layers. As a consequence, spin waves are emitted from the YIG/CoFeB interface and PSSWs form when their wave vector matches the perpendicular confinement condition. PSSWs are not excited when the exchange coupling between YIG and CoFeB is suppressed by a Ta spacer layer. Micromagnetic simulations confirm the exchange-torque mechanism.
The structures of epitaxial ultrathin Co2FeAl/MgO(001) heterostructures relating to the interface-induced perpendicular magnetic anisotropy (PMA) were investigated using scanning transmission electron microscopy, energy dispersive x-ray spectroscopy, and x-ray magnetic circular dichroism. We found that Al atoms from the Co2FeAl layer significantly interdiffuse into MgO, forming an Al-deficient Co-Fe-Al/Mg-Al-O structure near the Co2FeAl/MgO interface. This atomic replacement may play an additional role for enhancing PMA, which is consistent with the observed large perpendicular orbital magnetic moments of Fe atoms at the interface. This work suggests that control of interdiffusion at ferromanget/barrier interfaces is critical for designing an interface-induced PMA system.
Graphene is attractive for spintronics due to its long spin life time and high mobility. So far only thick and polycrystalline slabs have been used as ferromagnetic electrodes. We report the growth of flat, epitaxial ultrathin Co films on graphene. These display perpendicular magnetic anisotropy in the thickness range 0.5-1nm, which is confirmed by theory. PMA, epitaxy and ultrathin thickness bring new perspectives for graphene-based spintronic devices such as the zero-field control of an arbitrary magnetization direction, band matching between electrodes and graphene, and interface effects such as Rashba and electric field control of magnetism.