Register a new userIsotopic enrichment of silicon by high fluence $^{28}$Si$^-$ ion implantation
62
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
Spins in the `semiconductor vacuum of silicon-28 ($^{28}$Si) are suitable qubit candidates due to their long coherence times. An isotopically purified substrate of $^{28}$Si is required to limit the decoherence pathway caused by magnetic perturbations from surrounding $^{29}$Si nuclear spins (I=1/2), present in natural Si (nat Si) at an abundance of 4.67%. We isotopically enrich surface layers of nat Si by sputtering using high fluence $^{28}$Si$^-$ implantation. Phosphorus (P) donors implanted into one such $^{28}$Si layer with ~3000 ppm $^{29}$Si, produced by implanting 30 keV $^{28}$Si$^-$ ions at a fluence of 4x10^18 cm^-2, were measured with pulsed electron spin resonance, confirming successful donor activation upon annealing. The mono-exponential decay of the Hahn echo signal indicates a depletion of $^{29}$Si. A coherence time of T2 = 285 +/- 14 us is extracted, which is longer than that obtained in nat Si for similar doping concentrations and can be increased by reducing the P concentration in future. The isotopic enrichment was improved by employing one-for-one ion sputtering using 45 keV $^{28}$Si$^-$ implantation. A fluence of 2.63x10^18 cm^-2 $^{28}$Si$^-$ ions were implanted at this energy into nat Si, resulting in an isotopically enriched surface layer ~100 nm thick; suitable for providing a sufficient volume of $^{28}$Si for donor qubits implanted into the near-surface region. We observe a depletion of $^{29}$Si to 250 ppm as measured by secondary ion mass spectrometry. The impurity content and the crystallization kinetics via solid phase epitaxy are discussed. The $^{28}$Si layer is confirmed to be a single crystal using transmission electron microscopy. This method of Si isotopic enrichment shows promise for incorporating into the fabrication process flow of Si spin qubit devices.
rate research
Read More
In this paper, we discuss the results of our study of the synthesis of endohedral iron-fullerenes. A low energy Fe+ ion beam was irradiated to C60 thin film by using a deceleration system. Fe+-irradiated C60 thin film was analyzed by high performance liquid chromatography and laser desorption/ionization time-of-flight mass spectrometry. We investigated the performance of the deceleration system for using a Fe+ beam with low energy. In addition, we attempted to isolate the synthesized material from a Fe+-irradiated C60 thin film by high performance liquid chromatography.
X-ray photoelectron spectroscopy (XPS) and resonant x-ray emission spectroscopy (RXES) measurements of pellet and thin film forms of TiO$_2$ with implanted Fe ions are presented and discussed. The findings indicate that Fe-implantation in a TiO$_2$ pellet sample induces heterovalent cation substitution (Fe$^{2+}rightarrow$ Ti$^{4+}$) beneath the surface region. But in thin film samples, the clustering of Fe atoms is primarily detected. In addition to this, significant amounts of secondary phases of Fe$^{3+}$ are detected on the surface of all doped samples due to oxygen exposure. These experimental findings are compared with density functional theory (DFT) calculations of formation energies for different configurations of structural defects in the implanted TiO$_2$:Fe system. According to our calculations, the clustering of Fe-atoms in TiO$_2$:Fe thin films can be attributed to the formation of combined substitutional and interstitial defects. Further, the differences due to Fe doping in pellet and thin film samples can ultimately be attributed to different surface to volume ratios.
An additional value of the Avogadro constant was obtained by counting the atoms in isotopically enriched Si spheres. With respect to the previous determination, the spheres were etched and repolished to eliminate metal contaminations and to improve the roundness. In addition, all the input quantities -- molar mass, lattice parameter, mass, and volume -- were remeasured aiming at a smaller uncertainty. In order to make the values given Refs. 1 and 2 usable for a least squares adjustment, we report about the estimate of their correlation.
This is the abstract. The results of measurements of X-ray photoelectron spectra (XPS) of a-SiO2-host material after pulsed implantation with [Mn+] and [Co+, Mn+]-ions as well as DFT-calculations are presented. The low-energy shift is found in XPS Si 2p and O 1s core-levels of single [Mn+] and dual [Co+, Mn+] pulsed ion-implanted a-SiO2 (E = 30 keV, D = 2*10^17 cm^-2) with respect to those of untreated a-SiO2.The similar changes are found in XPS Si 2p and O 1s of stishovite compared to those of quartz. This means that the pulsed ion-implantation induces the local high pressure effect which leads to an appearance of SiO6-structural units in alpha-SiO2 host, forming stishovite-like local atomic structure. This process can be described within electronic bonding transition from the four-fold quartz-like to six-fold stishovite-like high-pressure phase in SiO2 host-matrix. It is found that such octahedral conversion depends on the fluence and starts with doses higher than D = 3*10^16 cm^-2.
Silicon is host to two separate leading quantum technology platforms: integrated silicon photonics as well as long-lived spin qubits. There is an ongoing search for the ideal photon-spin interface able to hybridize these two approaches into a single silicon platform offering substantially expanded capabilities. A number of silicon defects are known to have spin-selective optical transitions, although very few of these are known to be in the highly desirable telecommunications bands, and those that do often do not couple strongly to light. Here we characterize the T center in silicon, a highly stable silicon defect which supports a short-lived bound exciton that upon recombination emits light in the telecommunications O-band. In this first study of T centers in $^{28}$Si, we present the temperature dependence of the zero phonon line, report ensemble zero phonon linewidths as narrow as 33(2) MHz, and elucidate the excited state spectrum of the bound exciton. Magneto-photoluminescence, in conjunction with magnetic resonance, is used to observe twelve distinct orientational subsets of the T center, which are independently addressable due to the anisotropic g factor of the bound excitons hole spin. The T center is thus a promising contender for the hybridization of silicons two leading quantum technology platforms.