We present two prescriptions for broadband (~77 - 252 GHz), millimeter-wave antireflection coatings for cryogenic, sintered polycrystalline aluminum oxide optics: one for large-format (700 mm diameter) planar and plano-convex elements, the other for densely packed arrays of quasi-optical elements, in our case 5 mm diameter half-spheres (called lenslets). The coatings comprise three layers of commercially-available, polytetrafluoroethylene-based, dielectric sheet material. The lenslet coating is molded to fit the 150 mm diameter arrays directly while the large-diameter lenses are coated using a tiled approach. We review the fabrication processes for both prescriptions then discuss laboratory measurements of their transmittance and reflectance. In addition, we present the inferred refractive indices and loss tangents for the coating materials and the aluminum oxide substrate. We find that at 150 GHz and 300 K the large-format coating sample achieves (97 +/- 2)% transmittance and the lenslet coating sample achieves (94 +/- 3)% transmittance.
rate research
Read More
We have developed and tested an antireflection (AR) coating method for silicon lenses at cryogenic temperatures and millimeter wavelengths. Our particular application is a measurement of the cosmic microwave background. The coating consists of machined pieces of Cirlex glued to the silicon. The measured reflection from an AR coated flat piece is less than 1.5% at the design wavelength. The coating has been applied to flats and lenses and has survived multiple thermal cycles from 300 to 4 K. We present the manufacturing method, the material properties, the tests performed, and estimates of the loss that can be achieved in practical lenses.
Thermal Kinetic Inductance Detectors (TKIDs) combine the excellent noise performance of traditional bolometers with a radio frequency multiplexing architecture that enables the large detector counts needed for the next generation of millimeter-wave instruments. In this paper, we first discuss the expected noise sources in TKIDs and derive the limits where the phonon noise contribution dominates over the other detector noise terms: generation-recombination, amplifier, and two-level system (TLS) noise. Second, we characterize aluminum TKIDs in a dark environment. We present measurements of TKID resonators with quality factors of about $10^5$ at 80 mK. We also discuss the bolometer thermal conductance, heat capacity, and time constants. These were measured by the use of a resistor on the thermal island to excite the bolometers. These dark aluminum TKIDs demonstrate a noise equivalent power NEP = $2 times 10^{-17} mathrm{W}/mathrm{sqrt{Hz}} $, with a $1/f$ knee at 0.1 Hz, which provides background noise limited performance for ground-based telescopes observing at 150 GHz.
The detection of VUV scintillation light, e.g. in (liquid) argon detectors, commonly includes a reflector with a fluorescent coating, converting UV photons to visible light. The light yield of these detectors depends directly on the conversion efficiency. Several coating/reflector combinations were produced using VM2000, a specular reflecting multi layer polymer, and Tetratex, a diffuse reflecting PTFE fabric, as reflector foils. The light yield of these coatings was optimised and has been measured in a dedicated liquid argon setup built at the University of Zurich. It employs a small, 1.3 kg LAr cell viewed by a 3-inch, low radioactivity PMT of type R11065-10 from Hamamatsu. The cryogenic stability of these coatings was additionally studied. The optimum reflector/coating combination was found to be Tetratex dip coated with Tetraphenyl-butadiene with a thickness of 0.9 mg/cm$^2$ resulting in a 3.6 times higher light yield compared to uncoated VM2000. Its performance was stable in long term measurements, ran up to 100 days, in liquid argon. This coated reflector was further investigated concerning radioactive impurities found to be suitable for current and upcoming low-background experiments. Therefore it is used for the liquid argon veto in Phase II of the GERDA neutrinoless double beta decay experiment.
Broadband refractive optics realized from high index materials provide compelling design solutions for the next generation of observatories for the Cosmic Microwave Background (CMB), and for sub-millimeter astronomy. In this paper, work is presented which extends the state of the art in silicon lenses with metamaterial antireflection (AR) coatings towards larger bandwidth and higher frequency operation. Examples presented include octave bandwidth coatings with less than $0.5%$ reflection, a prototype 4:1 bandwidth coating, and a coating optimized for 1.4 THz. For these coatings the detailed design, fabrication and testing processes are described as well as the inherent performance trade offs.
We used two novel approaches to produce sub-wavelength structure (SWS) anti-reflection coatings (ARC) on silicon for the millimeter and sub-millimeter (MSM) wave band: picosecond laser ablation and dicing with beveled saws. We produced pyramidal structures with both techniques. The diced sample, machined on only one side, had pitch and height of 350 $mu$m and 972 $mu$m. The two laser ablated samples had pitch of 180 $mu$m and heights of 720 $mu$m and 580 $mu$m; only one of these samples was ablated on both sides. We present measurements of shape and optical performance as well as comparisons to the optical performance predicted using finite element analysis and rigorous coupled wave analysis. By extending the measured performance of the one-sided diced sample to the two-sided case, we demonstrate 25 % band averaged reflectance of less than 5 % over a bandwidth of 97 % centered on 170 GHz. Using the two-sided laser ablation sample, we demonstrate reflectance less than 5 % over 83 % bandwidth centered on 346 GHz.