Register a new userSuperconductivity behavior in epitaxial TiN films points at surface magnetic disorder
94
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
We analyze the evolution of the normal and superconducting electronic properties in epitaxial TiN films, characterized by high Ioffe-Regel parameter values, as a function of the film thickness. As the film thickness decreases, we observe an increase of in the residual resistivity, which becomes dominated by diffusive surface scattering for $dleq20,$nm. At the same time, a substantial thickness-dependent reduction of the superconducting critical temperature is observed compared to the bulk TiN value. In such a high quality material films, this effect can be explained by a weak magnetic disorder residing in the surface layer with a characteristic magnetic defect density of $sim10^{12},mathrm{cm}^{-2}$. Our results suggest that surface magnetic disorder is generally present in oxidized TiN films.
rate research
Read More
Despite the low resistivity (~ 1 mohm cm), the metallic electrical transport has not been commonly observed in the inverse spinel NiCo2O4, except in certain epitaxial thin films. Previous studies have stressed the effect of valence mixing and degree of spinel inversion on the electric conduction of NiCo2O4 films. In this work, we have studied the effect of microstructure by comparing the NiCo2O4 epitaxial films grown on MgAl2O4 (111) and on Al2O3 (0001) substrates. Although the optimal growth condition and the magnetic properties are similar for the NiCo2O4/MgAl2O4 and the NiCo2O4/Al2O3, they show metallic and semiconducting electrical transport respectively. Despite similar temperature and field dependence of magnetization, the NiCo2O4/Al2O3 show much larger magnetoresistance at low temperature. Post-growth annealing decreases the resistivity of NiCo2O4/Al2O3, but the annealed films are still semiconducting. The correlation between the structural correlation length and the resistivity suggests that the microstructural disorder, generated by the dramatic mismatch between the NiCo2O4 and Al2O3 crystal structures, may be the origin of the absence of the metallic electrical transport in NiCo2O4. These results reveal microstructural disorder as another key factor in controlling the electrical transport of NiCo2O4, with potentially large magnetoresistance for spintronics application.
Titanium nitride (TiN) is a paradigm of refractory transition metal nitrides with great potential in vast applications. Generally, the plasmonic performance of TiN can be tuned by oxidation, which was thought to be only temperature-, oxygen partial pressure-, and time-dependent. Regarding the role of crystallographic orientation in the oxidation and resultant optical properties of TiN films, little is known thus far. Here we reveal that both the oxidation resistance behavior and the plasmonic performance of epitaxial TiN films follow the order of (001) < (110) < (111). The effects of crystallographic orientation on the lattice constants, optical properties, and oxidation levels of epitaxial TiN films have been systematically studied by combined high-resolution X-ray diffraction, spectroscopic ellipsometry, X-ray absorption spectroscopy, and X-ray photoemission spectroscopy. To further understand the role of crystallographic orientation in the initial oxidation process of TiN films, density-functional-theory calculations are carried out, indicating the energy cost of oxidation is (001) < (110) < (111), consistent with the experiments. The superior endurance of the (111) orientation against mild oxidation can largely alleviate the previously stringent technical requirements for the growth of TiN films with high plasmonic performance. The crystallographic orientation can also offer an effective controlling parameter to design TiN-based plasmonic devices with desired peculiarity, e.g., superior chemical stability against mild oxidation or large optical tunability upon oxidation.
Epitaxial titanium diboride thin films have been deposited on sapphire substrates by Pulsed Laser Ablation technique. Structural properties of the films have been studied during the growth by Reflection High Energy Electron Diffraction (RHEED) and ex-situ by means of X-ray diffraction techniques; both kinds of measurements indicate a good crystallographic orientation of the TiB2 film both in plane and along the c axis. A flat surface has been observed by Atomic Force Microscopy imaging. Electrical resistivity at room temperature resulted to be five times higher than the value reported for single crystals. The films resulted to be also very stable at high temperature, which is very promising for using this material as a buffer layer in the growth of magnesium diboride thin films.
We report a giant resistance drop induced by dc electrical currents in La0.67Ca0.33MnO3 epitaxial thin films. Resistance of the patterned thin films decreases exponentially with increasing current and a maximum drop shows at the temperature of resistance peak Tp. Variation of resistance with current densities can be scaled below and above Tp, respectively. This work can be useful for the future applications of electroresistance.
We report the observation of spin-glass-like behavior and strong magnetic anisotropy in extremely smooth (~1-3 AA) roughness) epitaxial (110) and (010) SrRuO3 thin films. The easy axis of magnetization is always perpendicular to the plane of the film (unidirectional) irrespective of crystallographic orientation. An attempt has been made to understand the nature and origin of spin-glass behavior, which fits well with Heisenberg model.
Log in to be able to interact and post comments
comments
Fetching comments
Sign in to be able to follow your search criteria