Register a new userSystematic study of the electronic structure and the magnetic properties of a few-nm-thick epitaxial (Ni1-xCox)Fe2O4 (x = 0 - 1) layers grown on Al2O3(111)/Si(111) using soft X-ray magnetic circular dichroism: effects of cation distribution
59
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
We study the electronic structure and the magnetic properties of epitaxial (Ni1-xCox)Fe2O4(111) layers (x = 0 - 1) with thicknesses d = 1.7 - 5.2 nm grown on Al2O3(111)/Si(111) structures, to achieve a high value of inversion parameter y, which is the inverse-to-normal spinel-structure ratio, and hence to obtain good magnetic properties even when the thickness is thin enough for electron tunneling as a spin filter. We revealed the crystallographic (octahedral Oh or tetrahedral Td) sites and the valences of the Fe, Co, and Ni cations using experimental soft X-ray absorption spectroscopy and X-ray magnetic circular dichroism spectra and configuration-interaction cluster-model calculation. In all the (Ni1-xCox)Fe2O4 layers with d = about 4 nm, all Ni cations occupy the Ni2+ (Oh) site, whereas Co cations occupy the three different Co2+ (Oh), Co2+ (Td), and Co3+ (Oh) sites with constant occupancies. According to these features, the occupancy of the Fe3+ (Oh) cations decreases and that of the Fe3+ (Td) cations increases with decreasing x. Consequently, we obtained a systematic increase of y with decreasing x and achieved the highest y value of 0.91 for the NiFe2O4 layer with d = 3.5 nm. From the d dependences of y and magnetization in the d range of 1.7 - 5.2 nm, a magnetically dead layer is present near the NiFe2O4/Al2O3 interface, but its influence on the magnetization was significantly suppressed compared with the case of CoFe2O4 layers reported previously [Y. K. Wakabayasi et al., Phys. Rev. B 96, 104410 (2017)], due to the high site selectivity of the Ni cations. Since our epitaxial NiFe2O4 layer with d = 3.5 nm has a high y values (0.91) and a reasonably large magnetization (180 emu/cc), it is expected to exhibit a strong spin filter effect, which can be used for efficient spin injection into Si.
rate research
Read More
We have studied in-gap states in epitaxial CoFe2O4(111), which potentially acts as a perfect spin filter, grown on a Al2O3(111)/Si(111) structure by using ellipsometry, Fe L2,3-edge x-ray absorption spectroscopy (XAS), and Fe L2,3-edge resonant inelastic x-ray scattering (RIXS), and revealed the relation between the in-gap states and chemical defects due to the Fe2+ cations at the octahedral sites (Fe2+ (Oh) cations). The ellipsometry measurements showed the indirect band gap of 1.24 eV for the CoFe2O4 layer and the Fe L2,3-edge XAS confirmed the characteristic photon energy for the preferential excitation of the Fe2+ (Oh) cations. In the Fe L3-edge RIXS spectra, a band-gap excitation and an excitation whose energy is smaller than the band-gap energy (Eg = 1.24 eV) of CoF2O4, which we refer to as below-band-gap excitation (BBGE) hereafter, were observed. The intensity of the BBGE was strengthened at the preferential excitation energy of the Fe2+ (Oh) cations. In addition, the intensity of the BBGE was significantly increased when the thickness of the CoFe2O4 layer was decreased from 11 to 1.4 nm, which coincides with the increase in the site occupancy of the Fe2+ (Oh) cations with decreasing the thickness. These results indicate that the BBGE comes from the in-gap states of the Fe2+ (Oh) cations whose density increases near the heterointerface on the bottom Al2O3 layer. We have demonstrated that RIXS measurements and analyses in combination with ellipsometry and XAS are effective to provide an insight into in-gap states in thin-film oxide heterostructures.
The spin and orbital magnetic moments of the Fe3O4 epitaxial ultrathin film synthesized by plasma assisted simultaneous oxidization on MgO(100) have been studied with X-ray magnetic circular dichroism (XMCD). The ultrathin film retains a rather large total magnetic moment, i.e. (2.7+-0.15) uB/f.u., which is ~ 70% of that for the bulk-like Fe3O4. A significant unquenched orbital moment up to (0.54+-0.05) uB/f.u. was observed, which could come from the symmetry breaking at the Fe3O4/MgO interface. Such sizable orbital moment will add capacities to the Fe3O4-based spintronics devices in the magnetization reversal by the electric field.
We performed a soft x-ray magnetic circular dichroism (XMCD) study of a Zn$_{1-x}$V$_x$O thin film which showed small ferromagnetic moment. Field and temperature dependences of V 2$p$ XMCD signals indicated the coexistence of Curie-Weiss paramagnetic, antiferromagnetic, and possibly ferromagnetic V ions, quantitatively consistent with the magnetization measurements. We attribute the paramagnetic signal to V ions substituting Zn sites which are somewhat elongated along the c-axis.
The magnetic properties of as-grown Ga$_{1-x}$Mn$_{x}$As have been investigated by the systematic measurements of temperature and magnetic field dependent soft x-ray magnetic circular dichroism (XMCD). The {it intrinsic} XMCD intensity at high temperatures obeys the Curie-Weiss law, but residual spin magnetic moment appears already around 100 K, significantly above Curie temperature ($T_C$), suggesting that short-range ferromagnetic correlations are developed above $T_C$. The present results also suggest that antiferromagnetic interaction between the substitutional and interstitial Mn (Mn$_{int}$) ions exists and that the amount of the Mn$_{int}$ affects $T_C$.
Taking advantage of the large electron escape depth of soft x-ray angle resolved photoemission spectroscopy we report electronic structure measurements of (111)-oriented [LaNiO3/LaMnO3] superlattices and LaNiO3 epitaxial films. For thin films we observe a 3D Fermi surface with an electron pocket at the Brillouin zone center and hole pockets at the zone vertices. Superlattices with thick nickelate layers present a similar electronic structure. However, as the thickness of the LaNiO3 is reduced the superlattices become insulating. These heterostructures do not show a marked redistribution of spectral weight in momentum space but exhibit a pseudogap of 50 meV.