Single crystal growth of {alpha}-Na$_x$MnO$_2$ (x = 0.90) is reported via the floating zone technique. The conditions required for stable growth and intergrowth-free crystals are described along with the results of trials under alternate growth atmospheres. Chemical and structural characterizations of the resulting {alpha}-Na$_{0.90}$MnO$_2$ crystals are performed using ICP-AES, NMR, XANES, XPS, and neutron diffraction measurements. As a layered transition metal oxide with large ionic mobility and strong correlation effects, {alpha}-Na$_x$MnO$_2$ is of interest to many communities, and the implications of large volume, high purity, single crystal growth are discussed.
rate research
Read More
The perovskite SrVO$_3$ is of interest for a variety of applications due to its simple metallic character and stability in reducing environments. Here we report the preparation of single-crystal SrVO$_3$ using the laser floating zone technique. Laue diffraction implies single domains ca. 30 mm in length. The stoichiometry of optimized crystals was found to be Sr$_{0.985}$VO$_{2.91}$ using inductively coupled plasma optical emission spectrometry and neutron powder diffraction analysis, with compositions adjustable depending on the crystal pulling rate. Heat capacity measurements from 2 to 300 K show variations with composition, attributable to a combination of impurity scattering and changes in phonon dynamics.Our results demonstrate the utility of the laser floating zone technique in preparing a range of materials, and our advances with SrVO$_3$ may help lead to applications including catalysis, transparent conducting oxides, thermionic emitters, and other electronic devices.
We report the growth of large single-crystals of Cu2MnAl, a ferromagnetic Heusler compound suitable for polarizing neutron monochromators, by means of optical floating zone under ultra-high vacuum compatible conditions. Unlike Bridgman or Czochralsky grown Cu2MnAl, our floating zone grown single-crystals show highly reproducible magnetic properties and an excellent crystal quality with a narrow and homogeneous mosaic spread as examined by neutron diffraction. An investigation of the polarizing properties in neutron scattering suggests a high polarization efficiency, limited by the relatively small sample dimensions studied. Our study identifies optical floating zone under ultra-high vacuum compatible conditions as a highly reproducible method to grow high-quality single-crystals of Cu2MnAl.
We report a systematic study on the crystal growth of the rare-earth titanates $R_2$Ti$_2$O$_7$ ($R$ = Gd, Tb, Dy, Ho, Y, Er, Yb and Lu) and Y-doped Tb$_{2-x}$Y$_x$Ti$_2$O$_7$ ($x$ = 0.2 and 1) using an optical floating-zone method. High-quality single crystals were successfully obtained and the growth conditions were carefully optimized. The oxygen pressure was found to be the most important parameter and the appropriate ones are 0.1--0.4 MPa, depending on the radius of rare-earth ions. The growth rate is another parameter and was found to be 2.5--4 mm/h for different rare-earth ions. X-ray diffraction data demonstrated the good crystallinity of these crystals. The basic physical properties of these crystals were characterized by the magnetic susceptibility and specific heat measurements.
Recent theoretical and experimental findings suggest that the long-known but not well understood low temperature resistance plateau of SmB6 may originate from protected surface states arising from a topologically non-trivial bulk band structure having strong Kondo hybridization. Yet other studies have ascribed this feature to impurity phases, sample vacancies, and surface reconstructions. Given the typical methods used to prepare SmB6 single crystals, the flux and floating zone procedures, these ascriptions should not be taken lightly. Here, we demonstrate how compositional variations and observable amounts of impurity phases in SmB6 crystals grown by floating zone and flux affect the physical properties. From neutron diffraction and X-ray computed tomography experiments, we observe that a 154Sm11B6 crystal prepared using aluminum flux contains co-crystallized, epitaxial aluminum. A large, nearly stoichiometric crystal of SmB6 was successfully grown using the float-zone technique; upon continuing the zone melting, samarium vacancies are introduced. These samarium vacancies drastically alter the resistance and plateauing magnitude of the low temperature resistance compared to stoichiometric SmB6. These results highlight that small presences of impurity phases and compositional variations must be considered when collecting and analyzing physical property data of SmB6. Finally, a more accurate samarium-154 coherent neutron scattering length value, 8.9(1) fm, is reported.
We report the optimized conditions for growing the high quality single crystals of candidate quantum spin-ice Pr2Hf2O7 using the optical floating-zone method. Large single crystals of Pr2Hf2O7 have been grown under different growth conditions using a four-mirror type optical floating-zone furnace and their microscopic structural differences have been probed by high-resolution synchrotron x-ray diffraction (SXRD). The SXRD data reveal that the crystals grown under fowing argon (~ 2 L/h) atmosphere with slightly off-stoichiometric (optimized) starting composition yields the highest quality crystals. The magnetic susceptibility, isothermal magnetization and heat capacity data of optimally grown crystals are presented.