Register a new userCharacteristics of Nickel Thin Film and Formation of Nickel Silicide by Remote Plasma Atomic Layer Deposition using Ni(iPr-DAD)2
228
0
0.0
(
0
)
Ask ChatGPT about the research
No Arabic abstract
In this study, the characteristics of nickel thin film deposited by remote plasma atomic layer deposition (RPALD) on p-type Si substrate and formation of nickel silicide using rapid thermal annealing were determined. Bis(1,4-di-isopropyl-1,3-diazabutadienyl)nickel, Ni(iPr-DAD)2, was used as a Ni precursor and ammonia plasma was used as a reactant. This was the first attempt to deposit Ni thin film using Ni(iPr-DAD)2 as a precursor for the ALD process. The RPALD Ni film was deposited with a growth rate of around 2.2{AA}/cycle at 250 {deg}C and showed significant low resistivity of 33 {mu}{Omega}cm with a total impurity concentration of around 10 at. %.The impurities of the thin film, carbon and nitrogen, were existent by the forms of C-C and C-N in a bonding state. The impurities removal tendency was investigated by comparing of experimental conditions, namely process temperature and pressure. Nitrogen impurity was removed by thermal desorption during each ALD cycle and carbon impurity was reduced by the optimizing of the process pressure which is directly related with a mean free path of NH3 plasma. After Ni deposition, nickel silicide was formed by RTA in a vacuum ambient for 1 minute. A nickel silicide layer from ALD Ni and PVD Ni was compared at the annealing temperature from 500 to 900 {deg}C. NiSi from ALD Ni showed better thermal stability due to the contribution of small amounts of carbon and nitrogen in the asdeposited Ni thin film. Degradation of the silicide layer was effectively suppressed with a use of ALD Ni.
rate research
Read More
Ordered arrays of magnetic nanowires are commonly synthesized by electrodeposition in nanoporous alumina templates. Due to their dense packing, strong magnetostatic interactions prevent the manipulation of wires individually. Using atomic layer deposition we reduce the diameter of the pores prior to electrodeposition. This reduces magnetostatic interactions, yielding fully remanent hysteresis loops. This is a first step towards the use of such arrays for magnetic racetrack memories.
Using low energy electron diffraction (LEED), Auger electron spectroscopy (AES), scanning tunnelling microscopy (STM) and high resolution photo-electron spectroscopy (HR-PES) techniques we have studied the annealing effect of one silicon monolayer deposited at room temperature onto a Ni (111) substrate. The variations of the Si surface concentration, recorded by AES at 300{deg}C and 400{deg}C, show at the beginning a rapid Si decreasing followed by a slowing down up to a plateau equivalent to about 1/3 silicon monolayer. STM images and LEED patterns, both recorded at room temperature just after annealing, reveal the formation of an ordered hexagonal superstructure(rot3xrot3)R30{deg}-type. From these observations and from a quantitative analysis of HR-PES data, recorded before and after annealing, we propose that the (rot3 x rot3)R30{deg}superstructure corresponds to a two dimensional (2D) Ni2Si surface silicide.
We report plasma-enhanced atomic layer deposition (ALD) to prepare conformal nickel thin films and nanotubes by using nickelocene as a precursor, water as the oxidant agent and an in-cycle plasma enhanced reduction step with hydrogen. The optimized ALD pulse sequence, combined with a post-processing annealing treatment, allowed us to prepare 30 nm thick metallic Ni layers with a resistivity of 8 $muOmega$cm at room temperature and good conformality both on the planar substrates and nanotemplates. Thereby we fabricated several micrometer-long nickel nanotubes with diameters ranging from 120 to 330 nm. We report on the correlation between ALD growth and functional properties of individual Ni nanotubes characterized in terms of magneto-transport and the confinement of spin wave modes. The findings offer novel perspectives for Ni-based spintronics and magnonic devices operated in the GHz frequency regime with a 3D device architecture.
The development of new electrochromic materials and devices, like smart windows, has an enormous impact on the energy efficiency of modern society. One of the crucial materials in this technology is nickel-oxide. Ni-deficient NiO shows anodic electrochromism whose mechanism is still under debate. Using DFT+U calculations, we show that Ni vacancy generation results in the formation of hole polarons localised at the two oxygens next to the vacancy. Upon Li insertion or injection of an extra electron into Ni-deficient NiO, one hole gets filled, and the hole bipolaron is converted into a hole polaron well-localized at one O atom. Furthermore, the calculated absorption coefficients demonstrate that Li insertion/extraction or rather the addition/removal of an extra electron into Ni-deficient NiO can lead to switching between the oxidized (colored) and the reduced (bleached) states. Hence, our results suggest a new mechanism of Ni-deficient NiO electrochromism not related to the Ni2+/Ni3+ transition but based on the formation and annihilation of hole polarons in oxygen p-states.
Fabrication of single nickel-nitrogen (NE8) defect centers in diamond by chemical vapor deposition is demonstrated. Under continuous-wave 745 nm laser excitation single defects were induced to emit single photon pulses at 797 nm with a linewidth of 1.5 nm at room temperature. Photon antibunching of single centers was demonstrated using a Hanbury-Brown and Twiss interferometer. Confocal images revealed approximately 10^6 optically active sites/cm^2 in the synthesized films. The fabrication of an NE8 based single photon source in synthetic diamond is important for fiber based quantum cryptography. It can also be used as an ideal point-like source for near-field optical microscopy.
Log in to be able to interact and post comments
comments
Fetching comments
Sign in to be able to follow your search criteria