First thermoelectric properties measurements on bulk nanostructured Ba8Ga16Ge30 clathrate-I are presented. A sol-gel-calcination route was developed for preparing amorphous nanosized precursor oxides. The further reduction of the oxides led to quantitative yield of crystalline nanosized Ba8Ga16Ge30 clathrate-I. TEM investigations show the clathrate nanoparticles retain the size and morphology of the precursor oxides. The clathrate nanoparticles contain mainly thin plates (approx. 300 nm x 300 nm x 50 nm) and a small amount of nanospheres (diameter ~ 10 nm). SAED patterns confirm the clathrate-I structure type for both morphologies. The powders were compacted via Spark Plasma Sintering (SPS) to obtain a bulk nano-structured material. The Seebeck coefficient S, measured on low-density samples (53% of {delta}x-ray), reaches -145 {mu}V/k at 375 {deg}C. The ZT values are quite low (0.02) due to the high resistivity of the sample (two orders of magnitude larger than bulk materials) and the low sample density. The trend of the temperature dependence of S is in agreement with the values obtained from electronic structure calculations and semi-classical Boltzmann transport theory within the constant scattering approximation. The total thermal conductivity (1.61 W/mK), measured on high density samples (93% of {delta}x-ray), shows a reduction of 20-25% in relation to the bulk materials (2.1 W/mK). A further shaping of the sample for the Seebeck coefficient and electrical conductivity measurements was not possible due to the presence of cracks. An improvement on the design of the pressing tools, loading of the sample and profile of the applied pressure will enhance the mechanical stability of the samples. These investigations are now in progress.
rate research
Read More
Clathrates are lightweight, cage-like, fully-sp3 three dimensional (3D) structures that are experimentally-available for several host elements of the IV group. However, carbon clathrates are as yet hypothetical structures. Herein, the mechanical properties of Type-I-C46 Type-II-C34 and Type-H-C34 carbon clathrates are explored by first-principles calculations. It is revealed that those carbon clathrates show distinct anisotropic patterns in ideal tensile/shear strengths and critical tensile/shear strains, with maximum ideal tensile strength of Type-I carbon clathrate that is superior over that of diamond in <111> direction. However, it is identified isotropy in shear Youngs modulus, and in terms of tensile/shear Youngs moduli, they are sorted as Type-I > Type-II > Type-H carbon clathrates. There are distinct critical load-bearing bond configurations that explain their distinct mechanical behaviors. Moreover, those carbon clathrates are intrinsically indirect semiconductors, and their electronic properties can be greatly dictated by mechanical strain. Carbon clathrates can be potentially utilized as lightweight technically robust engineering metastructures and in electromechanical devices.
Intermetallic clathrates are candidate materials for thermoelectric applications above room temperature. Here we explore whether their intrinsically low lattice thermal conductivities can be further reduced by nanostructuring and whether this can further enhance their thermoelectric performance.}{As bulk nanostructuring routes we studied melt spinning and ball milling. To optimize the compaction process and/or stabilize the nanostructure we varied the process parameters, used additives, and studied clathrate-based composites. Initial results on clathate nanowires as simpler model nanostructures are also presented.
The ability to manufacture tailored graphene nanostructures is a key factor to fully exploit its enormous technological potential. We have investigated nanostructures created in graphene by swift heavy ion induced folding. For our experiments, single layers of graphene exfoliated on various substrates and freestanding graphene have been irradiated and analyzed by atomic force and high resolution transmission electron microscopy as well as Raman spectroscopy. We show that the dense electronic excitation in the wake of the traversing ion yields characteristic nanostructures each of which may be fabricated by choosing the proper irradiation conditions. These nanostructures include unique morphologies such as closed bilayer edges with a given chirality or nanopores within supported as well as freestanding graphene. The length and orientation of the nanopore, and thus of the associated closed bilayer edge, may be simply controlled by the direction of the incoming ion beam. In freestanding graphene, swift heavy ion irradiation induces extremely small openings, offering the possibility to perforate graphene membranes in a controlled way.
Type-I clathrate compounds have attracted a great deal of interest in connection with the search for efficient thermoelectric materials. These compounds constitute networked cages consisting of nano-scale tetrakaidecahedrons (14 hedrons) and dodecahedrons (12 hedrons), in which the group 1 or 2 elements in the periodic table are encaged as the so-called rattling guest atom. It is remarkable that, though these compounds have crystalline cubic-structure, they exhibit glass-like phonon thermal conductivity over the whole temperature range depending on the states of rattling guest atoms in the tetrakaidecahedron. In addition, these compounds show unusual glass-like specific heats and THz-frequency phonon dynamics, providing a remarkable broad peak almost identical to those observed in topologically disordered amorphous materials or structural glasses, the so-called Boson peak. An efficient thermoelectric effect is realized in compounds showing these glass-like characteristics. This decade, a number of experimental works dealing with type-I clathrate compounds have been published. These are diffraction experiments, thermal and spectroscopic experiments in addition to those based on heat and electronic transport. These form the raw materials for this article based on advances this decade. The subject of this article involves interesting phenomena from the viewpoint of not only physics but also from the view point of the practical problem of elaborating efficient thermoelectric materials. This review presents a survey of a wide range of experimental investigations of type-I clathrate compounds, together with a review of theoretical interpretations of the peculiar thermal and dynamic properties observed in these materials.
Permanent magnet materials require a high uniaxial magneto-crystalline anisotropy. Exchange coupling between small crystallites with easy-plane anisotropy induces an effective uniaxial anisotropy if arranged accordingly. Nanostructuring of materials with easy-plane anisotropy is an alternative way to create hard-magnetic materials. The coercivity increases with decreasing feature size. The resulting coercive field is about 12 percent of the anisotropy field for a crystal size of 3.4 times the Bloch parameter.