Cobalt carbide nanoparticles were processed using polyol reduction chemistry that offers high product yields in a cost effective single-step process. Particles are shown to be acicular in morphology and typically assembled as clusters with room temperature coercivities greater than 4 kOe and maximum energy products greater than 20 KJ/m3. Consisting of Co3C and Co2C phases, the ratio of phase volume, particle size, and particle morphology all play important roles in determining permanent magnet properties. Further, the acicular particle shape provides an enhancement to the coercivity via dipolar anisotropy energy as well as offering potential for particle alignment in nanocomposite cores. While Curie temperatures are near 510K at temperatures approaching 700 K the carbide powders experience an irreversible dissociation to metallic cobalt and carbon thus limiting operational temperatures to near room temperature.
Employing a new experimental technique to measure magnetoelectric response functions, we have measured the magnetoelectric effect in composite films of nano granular metallic iron in anatase titanium dioxide at temperatures below 50 K. A magnetoelectric resistance is defined as the ratio of a transverse voltage to bias current as a function of the magnetic field. In contrast to the anomalous Hall resistance measured above 50 K, the magnetoelectic resistance below 50 K is significantly larger and exhibits an even symmetry with respect to magnetic field reversal $Hto -H$. The measurement technique required attached electrodes in the plane of the film composite in order to measure voltage as a function of bias current and external magnetic field. To our knowledge, the composite films are unique in terms of showing magnetoelectric effects at low temperatures, $<$ 50 K, and anomalous Hall effects at high temperatures, $>$ 50 K.