Scalable, Dip-and-dry Fabrication of a Wide-Angle Plasmonic Selective Absorber for High-efficiency Solar-Thermal Energy Conversion


الملخص بالإنكليزية

A galvanic displacement reaction-based, room-temperature dip-and-dry technique is demonstrated for fabricating selectively solar-absorbing plasmonic nanostructure-coated foils (PNFs). The technique, which allows for facile tuning of the PNFs spectral reflectance to suit different radiative and thermal environments, yields PNFs which exhibit excellent, wide-angle solar absorptance (0.96 at 15{deg}, to 0.97 at 35{deg}, to 0.79 at 80{deg}) and low hemispherical thermal emittance (0.10) without the aid of antireflection coatings. The thermal emittance is on par with those of notable selective solar absorbers (SSAs) in the literature, while the wide-angle solar absorptance surpasses those of previously reported SSAs with comparable optical selectivities. In addition, the PNFs show promising mechanical and thermal stabilities at temperatures of up to 200{deg}C. Along with the performance of the PNFs, the simplicity, inexpensiveness and environment-friendliness of the dip-and-dry technique makes it an appealing alternative to current methods for fabricating selective solar absorbers.

تحميل البحث