Low damping and microstructural perfection of sub-40nm-thin yttrium iron garnet films grown by liquid phase epitaxy


الملخص بالإنكليزية

The field of magnon spintronics is experiencing an increasing interest in the development of solutions for spin-wave-based data transport and processing technologies that are complementary or alternative to modern CMOS architectures. Nanometer-thin yttrium iron garnet (YIG) films have been the gold standard for insulator-based spintronics to date, but a potential process technology that can deliver perfect, homogeneous large-diameter films is still lacking. We report that liquid phase epitaxy (LPE) enables the deposition of nanometer-thin YIG films with low ferromagnetic resonance losses and consistently high magnetic quality down to a thickness of 20 nm. The obtained epitaxial films are characterized by an ideal stoichiometry and perfect film lattices, which show neither significant compositional strain nor geometric mosaicity, but sharp interfaces. Their magneto-static and dynamic behavior is similar to that of single crystalline bulk YIG. We found, that the Gilbert damping coefficient alpha is independent of the film thickness and close to 1 x 10-4, and that together with an inhomogeneous peak-to-peak linewidth broadening of delta H0|| = 0.4 G, these values are among the lowest ever reported for YIG films with a thickness smaller than 40 nm. These results suggest, that nanometer-thin LPE films can be used to fabricate nano- and micro-scaled circuits with the required quality for magnonic devices. The LPE technique is easily scalable to YIG sample diameters of several inches.

تحميل البحث