Edge structures are highly relevant to the electronic, magnetic and catalytic properties of two-dimensional (2D) transition metal dichalcogenides (TMDs) and their one dimensional (1D) counterpart, i.e., nanoribbons, which should be precisely tailored for the desirable applications. In this work, we report the formation of novel Mo6S6 nanowire (NW) terminated edges in a monolayer molybdenum disulfide (MoS2) via an e-beam irradiation process combined with high temperature heating in a scanning transmission electron microscope (STEM). Atomic structures of NW terminated edges and the dynamic formation process were observed experimentally. Further analysis shows that NW terminated edge could form on both Mo-zigzag (ZZ) edge and S-ZZ edge which can exhibit even higher stability superior to the pristine zigzag (ZZ) and armchair (AC) edge. In addition, the analogous edge structures can be also formed in MoS2 nanoribbon and other TMDs material such as MoxW1-xSe2. We believe that the presence of these novel edge structures in 2D and 1D TMD materials may provide novel properties and new opportunities for their versatile applications including catalytic, spintronic and electronic devices.
تحميل البحث