The growth of Bi films deposited on both A and B faces of InAs(111) has been investigated by low-energy electron diffraction, scanning tunneling microscopy, and photoelectron spectroscopy using synchrotron radiation. The changes upon Bi deposition of the In 4d and Bi 5d5/2 photoelectron signals allow to get a comprehensive picture of the Bi/InAs(1 1 1) interface. From the initial stages the Bi growth on the A face (In-terminated InAs) is epitaxial, contrary to that on the B face (As- terminated InAs) that proceeds via the formation of islands. Angle-resolved photoelectron spectra show that the electronic structure of a $approx 10$~BL deposit on the A face is identical to that of bulk Bi, while more than $approx 30$ BL are needed for the B face. Both bulk and surface states are well accounted for by fully relativistic ab initio spin-resolved photoemission calculations.