Fiber networks below the isostatic point: fracture without stress concentration


الملخص بالإنكليزية

Crack nucleation is a ubiquitous phenomena during materials failure, because stress focuses on crack tips. It is known that exceptions to this general rule arise in the limit of strong disorder or vanishing mechanical stability, where stress distributes over a divergent length scale and the material displays diffusive damage. Here we show, using simulations, that a class of diluted lattices displays a new critical phase when they are below isostaticity, where stress never concentrates, damage always occurs over a divergent length scale, and catastrophic failure is avoided.