We report an investigation of temperature and IrMn layered thickness dependence of anomalous-Hall resistance (AHR), anisotropic magnetoresistance (AMR), and magnetization on Pt/Ir20Mn80/Y3Fe5O12 (Pt/IrMn/YIG) heterostructures. The magnitude of AHR is dramatically enhanced compared with Pt/YIG bilayers. The enhancement is much more profound at higher temperatures and peaks at the IrMn thickness of 3 nm. The observed spin-Hall magnetoresistance (SMR) in the temperature range of 10-300 K indicates that the spin current generated in the Pt layer can penetrate the entire thickness of the IrMn layer to interact with the YIG layer. The lack of conventional anisotropic magnetoresistance (CAMR) implies that the insertion of the IrMn layer between Pt and YIG efficiently suppresses the magnetic proximity effect (MPE) on induced Pt moments by YIG. Our results suggest that the dual roles of the InMn insertion in Pt/IrMn/YIG heterostructures are to block the MPE and to transport the spin current between Pt and YIG layers. We discuss possible mechanisms for the enhanced AHR.