We report synthesis, structural details and complete superconducting characterization of very recently discovered Nb2PdS5 new superconductor. The synthesized compound is crystallized in mono-clinic structure. Bulk superconductivity is seen in both magnetic susceptibility and electrical resistivity measurements with superconducting transition temperature (Tc) at 6K. The upper critical field (Hc2), being estimated from high field magneto-transport measure-ments is above 240kOe. The estimated Hc2(0) is clearly above the Pauli paramagnetic limit. Heat capacity measurements show clear transition with well defined peak at Tc, but with lower jump than as expected for a BCS type superconductor. The Sommerfield constant and Debye temperature as determined from low temperature fitting of heat capacity data are 32mJ/moleK2 and 263K respectively. Hall coefficients and resistivity in conjugation with electronic heat capacity indicates multiple gap superconductivity signatures in Nb2PdS5. We also studied the impact of hydrostatic pressure on superconductivity of Nb2PdS5 and found nearly no change in Tc for the given pressure range.
تحميل البحث