Transport and Magnetic properties of Fe1/3VSe2


الملخص بالإنكليزية

Electrical conductivity, thermopower and magnetic properties of Fe-intercalated Fe0.33VSe2 has been reported between 4.2K - 300K. We observe a first order transition in the resistivity of the sintered pellets around 160K on cooling. The electronic properties including the transitional hysteresis in the resistance anomaly (from 80K-160K) are found to be very sensitive to the structural details of the samples, which were prepared in different annealing conditions. The thermopower results on the sintered pellets are reported between 10K - 300K. The magnetic measurements between 2K - 300K and up to 14 Tesla field show the absence of any magnetic ordering in Fe0.33VSe2. The magnetic moment per Fe -atom at room temperature (between 1.4 to 1.7 Bohr Magneton) is much lower than in previously reported anti-ferromagnetic FeV2Se4. Furthermore, the Curie constant shows a rapid and continuous reduction and combined with the high field magnetization result at 2K suggests a rapid decrease in the paramagnetic moments on cooling to low temperatures and the absence of any magnetic order in Fe0.33VSe2 at low temperatures.

تحميل البحث