We report on significant flux pinning enhancement in MgB2/Fe tapes that has been easily obtained by a simple and cheap route using acetone as both an efficient ball-milling medium and liquid additive through the in situ method. Results showed that the highly reactive C released from the decomposition of the acetone substituted into B sites, accompanied by the grain refinement effect due to the acetone doping. At 4.2 K, the transport Jc for the 5 wt % acetone doped tapes sintered at 700C reached up to 2.4x10^4 A/cm^2 at 10 T, which is even higher than that of the nano-C added samples heated at 900C.