Bulk textured MgB_2 material of nearly full density showing a weak c-axis alignment of the hexagonal MgB_2 grains parallel to the pressure direction was obtained by hot deformation of a stoichiometric MgB_2 pellet prepared by a gas-solid reaction. The texture of the material was verified by comparing the x-ray diffraction patterns of the hot deformed material with isotropic MgB_2 powder. A small, but distinct anisotropy of the upper critical field up to Hc2^{a,b}/Hc2^{c}~1.2 depending on degree of texture was found by resistance and susceptibility measurements. No anisotropy of the critical current density determined from magnetization measurements was found for the textured material.
قيم البحث
اقرأ أيضاً
$MgB_2$ becomes superconducting just below 40 K. Whereas porous polycrystalline samples of $MgB_2$ can be synthesized from boron powders, in this letter we demonstrate that dense wires of $MgB_2$ can be prepared by exposing boron filaments to $Mg$ va
por. The resulting wires have a diameter of 160 ${mu}m$, are better than 80% dense and manifest the full $chi = -1/4{pi}$ shielding in the superconducting state. Temperature-dependent resistivity measurements indicate that $MgB_2$ is a highly conducting metal in the normal state with $rho (40 K)$ = 0.38 $mu Ohm$-$cm$. Using this value, an electronic mean free path, $l approx 600~AA$ can be estimated, indicating that $MgB_2$ wires are well within the clean limit. $T_c$, $H_{c2}(T)$, and $J_c$ data indicate that $MgB_2$ manifests comparable or better superconducting properties in dense wire form than it manifests as a sintered pellet.
Topological insulators are a new class of materials, that exhibit robust gapless surface states protected by time-reversal symmetry. The interplay between such symmetry-protected topological surface states and symmetry-broken states (e.g. superconduc
tivity) provides a platform for exploring novel quantum phenomena and new functionalities, such as 1D chiral or helical gapless Majorana fermions, and Majorana zero modes which may find application in fault-tolerant quantum computation. Inducing superconductivity on topological surface states is a prerequisite for their experimental realization. Here by growing high quality topological insulator Bi$_2$Se$_3$ films on a d-wave superconductor Bi$_2$Sr$_2$CaCu$_2$O$_{8+delta}$ using molecular beam epitaxy, we are able to induce high temperature superconductivity on the surface states of Bi$_2$Se$_3$ films with a large pairing gap up to 15 meV. Interestingly, distinct from the d-wave pairing of Bi$_2$Sr$_2$CaCu$_2$O$_{8+delta}$, the proximity-induced gap on the surface states is nearly isotropic and consistent with predominant s-wave pairing as revealed by angle-resolved photoemission spectroscopy. Our work could provide a critical step toward the realization of the long sought-after Majorana zero modes.
The flux flow resistivity associated with purely viscous motion of vortices in high-quality MgB_2 was measured by microwave surface impedance. Flux flow resistivity exhibits unusual field dependence with strong enhancement at low field, which is mark
edly different to conventional s-wave superconductors. A crossover field which separates two distinct flux flow regimes having different flux flow resistivity slopes was clearly observed in H//ab-plane. The unusual H-dependence indicates that two very differently sized superconducting gaps in MgB_2 manifest in the vortex dynamics and almost equally contribute to energy dissipation. The carrier scattering rate in two different bands is also discussed with the present results, compared to heat capacity and thermal conductivity results.
By using transport and magnetic measurement, the upper critical field $H_{c2}(T)$ and the irreversibility line $H_{irr}(T)$ has been determined. A big separation between $H_{c2}(0)$ and $H_{irr}(0)$ has been found showing the existence of a quantum v
ortex liquid state induced by quantum fluctuation of vortices in the new superconductor $MgB_2$. Further investigation on the magnetic relaxation shows that both the quantum tunneling and the thermally activated flux creep weakly depends on temperature. But when the melting field $H_{irr}$ is approached, a drastic rising of the relaxation rate is observed. This may imply that the melting of the vortex matter at a finite temperature is also induced by the quantum fluctuation of vortices.
By doping MgB_2 superconductor with SiC nano-particles, we have successfully introduced pinning sites directly into the crystal lattice of MgB_2 grains (intra-grain pinning). It became possible due to the combination of counter-balanced Si and C co-s
ubstitution for B, leading to a large number of intra-granular dislocations and the dispersed nano-size impurities induced by the substitution. The magnetic field dependence of the critical current density was significantly improved in a wide temperature range, whereas the transition temperature in the sample MgB_2(SiC)_x having x = 0.34, the highest doping level prepared, dropped only by 2.6 K.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها