We investigate the external hydrostatic pressure effect on the superconducting transition temperature (Tc) of new layered superconductors Bi4O4S3 and NdO0.5F0.5BiS2. Though the Tc is found to have moderate decrease from 4.8 K to 4.3 K (dTconset/dP = -0.28 K/GPa) for Bi4O4S3 superconductor, the same increases from 4.6 K to 5 K (dTconset/dP = 0.44 K/GPa) upto 1.31 GPa followed by a sudden decrease from 5 K to 4.7 K upto 1.75 GPa for NdO0.5F0.5BiS2 superconductor. The variation of Tc in these systems may be correlated to increase or decrease of the charge carriers in the density of states under externally applied pressure.
قيم البحث
اقرأ أيضاً
We report the electrical resistivity measurements under pressure for the recently discovered BiS2-based layered superconductors Bi4O4S3 and La(O,F)BiS2. In Bi4O4S3, the transition temperature Tc decreases monotonically without a distinct change in th
e metallic behavior in the normal state. In La(O,F)BiS2, on the other hand, Tc initially increases with increasing pressure and then decreases above ? 1 GPa. The semiconducting behavior in the normal state is suppressed markedly and monotonically, whereas the evolution of Tc is nonlinear. The strong suppression of the semiconducting behavior without doping in La(O,F)BiS2 suggests that the Fermi surface is located in the vicinity of some instability. In the present study, we elucidate that the superconductivity in the BiS2 layer favors the Fermi surface at the boundary between the semiconducting and metallic behaviors.
We study the impact of hydrostatic pressure on superconductivity of new BiS2 based layered REO0.5F0.5BiS2 (RE-La, Pr, and Nd) compounds through the measurements of dc electrical resistivity. The REO0.5F0.5BiS2 (RE-La, Pr and Nd) compounds synthesized
by solid state reaction route via vacuum encapsulation are crystallized in the tetragonal P4/nmm space group. At ambient pressure the superconducting transition onset temperatures are 2.7K, 3.5K and 4.5K which are enhanced substantially under external hydrostatic pressure to 10.5K, 7.8K and 7.5K for LaO0.5F0.5BiS2, PrO0.5F0.5BiS2 and NdO0.5F0.5BiS2 respectively at 1.68GPa. The normal state electrical resistivity decreases with applied pressure for REO0.5F0.5BiS2 (RE-La, Pr and Nd). The electrical resistivity under magnetic field and applied pressure has been measured to estimate upper critical field, the values of which are 15.9Tesla, 8.8Tesla and 8.2Tesla for LaO0.5F0.5BiS2, PrO0.5F0.5BiS2 and NdO0.5F0.5BiS2 compounds. Substantial enhancement of superconductivity under moderate pressures in studied new BiS2 based superconductors call for the attention of condensed matter physics community.
We report the sulfur isotope effect on transition temperature in a BiS2-based superconductor Bi4O4S3. Polycrystalline samples of Bi4O4S3 were prepared using 32S and 34S isotope chemicals. From magnetization analyses, the isotope exponent (aS) was est
imated as -0.1 < aS < 0.1. Although the Tc estimated from electrical resistivity was scattered as compared to those estimated from the magnetization, we observed no clear correlation between Tc and the isotope mass. The present results suggest that unconventional paring states are essential in Bi4O4S3.
Polycrystalline sample of the new layered superconductor Bi4O4S3 is successfully synthesized by solid-state reaction method by using Bi, S and Bi2O3 powders with one step reaction. The superconducting transition temperature (Tconset=4.5 K), the zero
resistance transition temperature (Tc0=4.07 K) and the diamagnetic transition temperature (4.02 K at H=10 Oe) were confirmed by electrical transport and magnetic measurements. Also, our results indicate a typical type II-superconductor behavior. In addition, a large thermoelectric effect was observed with a dimensionless thermoelectric figure of merit (ZT) of about 0.03 at 300K, indicating Bi4O4S3 can be a potential thermoelectric material.
We succeed in enhancement of a superconducting transition temperature (Tc) for NdO0.7F0.3BiS2 single crystal by partial substitution of Pb for Bi. The Tc increases with increasing Pb concentration until 6%. The maximum Tczero is 5.6 K, which is the h
ighest value among BiS2 based superconductors synthesized under an ambient pressure. Pb substitution for Bi induces lattice shrinkage along the c axis. These results reflect that superconductivity in this system is responsive to the lattice strain.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها