We investigate the effect of the laser parameters of pulsed laser deposition on the film stoichiometry and electronic properties of LaAlO_3/SrTiO_3 (001) heterostructures. The La/Al ratio in the LaAlO_3 films was varied over a wide range from 0.88 to 1.15, and was found to have a strong effect on the interface conductivity. In particular, the carrier density is modulated over more than two orders of magnitude. The film lattice expansion, caused by cation vacancies, is found to be the important functional parameter. These results can be understood to arise from the variations in the electrostatic boundary conditions, and their resolution, with stoichiometry.
Oxide heterostructures represent a unique playground for triggering the emergence of novel electronic states and for implementing new device concepts. The discovery of 2D conductivity at the $LaAlO_3/SrTiO_3$ interface has been linking for over a dec
We report the operation of LaAlO_3 / SrTiO_3 depletion mode top-gated junction field-effect transistors using a range of LaAlO_3 thicknesses as the top gate insulator. Gated Hall bars show near ideal transistor characteristics at room temperature wit
The effect of oxygen content on the magnetic and transport properties of the ferromagnetic Eu0.9Ca0.1BaCo2O5.5+{delta} has been carried out. Unlike the increase in TC with calcium content, paradoxally the TC value decreases with the increase in oxyge
We report on the temperature dependence of the $ZrTe_5$ electronic properties, studied at equilibrium and out of equilibrium, by means of time and angle resolved photoelectron spectroscopy. Our results unveil the dependence of the electronic band str
The electronic properties of the polar interface between insulating oxides is a subject of great current interest. An exciting new development is the observation of robust magnetism at the interface of two non-magnetic materials LaAlO_3 (LAO) and SrT