Neutron diffraction measurements have been carried out to investigate the magnetic form factor of the parent SrFe2As2 system of the iron-based superconductors. The general feature is that the form factor is approximately isotropic in wave vector, indicating that multiple d-orbitals of the iron atoms are occupied as expected based on band theory. Inversion of the diffraction data suggests that there is some elongation of the spin density toward the As atoms. We have also extended the diffraction measurements to investigate a possible jump in the c-axis lattice parameter at the structural phase transition, but find no detectable change within the experimental uncertainties.
قيم البحث
اقرأ أيضاً
We have performed neutron diffraction measurement on a single crystal of parent compound of iron-based superconductor, BaFe$_2$As$_2$ at 12~K. In order to investigate in-plane anisotropy of magnetic form factor in the antiferromagnetic phase, the det
winned single crystal is used in the measurement. The magnetic structure factor and magnetic form factor are well explained by the spin densities consisting of $3d_{yz}$ electrons with a fraction of about 40~% and the electrons in the other four $3d$ orbitals with each fraction of about 15~%. Such anisotropic magnetic form factor is qualitatively consistent with the anisotropic magnetic behaviors observed in the antiferromagnetic phase of the parent compound of iron-based superconductor.
We report inelastic neutron scattering studies of magnetic excitations in antiferromagnetically ordered SrFe$_{2}$As$_{2}$ ($T_{N}=220$ K), the parent compound of the FeAs-based superconductors. At low temperatures (T=7 K), the spectrum of magnetic e
xcitations $S(Q,hbar omega)$ consists of a Bragg peak at the elastic position ($hbar omega =0$ meV), a spin gap ($ Delta leq 6.5$ meV), and sharp spin wave excitations at higher energies. Based on the observed dispersion relation, we estimate the effective magnetic exchange coupling using a Heisenberg model. On warming across $T_{N} $, the low temperature spin gap rapidly closes, with weak critical scattering and spin-spin correlations in the paramagnetic state. The antiferromagnetic order in SrFe$_{2}$As$_{2}$ is therefore consistent with a first order phase transition, similar to the structural lattice distortion.
A detailed elastic neutron scattering study of the structural and magnetic phase transitions in single-crystal SrFe$_2$As$_2$ reveals that the orthorhombic (O)-tetragonal (T) and the antiferromagnetic transitions coincide at $T_texttt{O}$ = $T_texttt
{N}$ = (201.5 $pm$ 0.25) K. The observation of coexisting O-T phases over a finite temperature range at the transition and the sudden onset of the O distortion provide strong evidences that the structural transition is first order. The simultaneous appearance and disappearance within 0.5 K upon cooling and within 0.25 K upon warming, respectively, indicate that the magnetic and structural transitions are intimately coupled. We find that the hysteresis in the transition temperature extends over a 1-2 K range. Based on the observation of a remnant orthorhombic phase at temperatures higher than emph{T}$_texttt{O}$, we suggest that the T-O transition may be an order-disorder transition.
We have successfully grown high quality single crystals of SrFe$_2$As$_2$ and A$_{0.6}$K$_{0.4}$Fe$_2$As$_2$(A=Sr, Ba) using flux method. The resistivity, specific heat and Hall coefficient have been measured. For parent compound SrFe$_2$As$_2$, an a
nisotropic resistivity with $rho_c$ / $rho_{ab}$ as large as 130 is obtained at low temperatures. A sharp drop in both in-plane and out-plane resistivity due to the SDW instability is observed below 200 K. The angular dependence of in-plane magnetoresistance shows 2-fold symmetry with field rotating within ab plane below SDW transition temperature. This is consistent with a stripe-type spin ordering in SDW state. In K doped A$_{0.6}$K$_{0.4}$Fe$_2$As$_2$(A=Sr. Ba), the SDW instability is suppressed and the superconductivity appears with T$_c$ above 35 K. The rather low anisotropy in upper critical field between H$parallel$ab and H$parallel$c indicates inter-plane coupling play an important role in hole doped Fe-based superconductors.
In order to investigate whether magnetism and superconductivity coexist in Co-doped SrFe$_2$As$_2$, we have prepared single crystals of SrFe$_{2-x}$Co$_x$As$_2$, $x$ = 0 and 0.4, and characterized them via X-ray diffraction, electrical resistivity in
zero and applied field up to 9 T as well as at ambient and applied pressure up to 1.6 GPa, and magnetic susceptibility. At $x$ = 0.4, there is both magnetic and resistive evidence for a spin density wave transition at 120 K, while $T_c$ = 19.5 K - indicating coexistent magnetism and superconductivity. A discussion of how these results compare with reported results, both in SrFe$_{2-x}$Co$_x$As$_2$ and in other doped 122 compounds, is given.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها