تسجيل مستخدم جديدIon beam induced enhanced diffusion from gold thin films in silicon
225
0
0.0
(
0
)
تأليف
J. Ghatak
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Enhanced diffusion of gold atoms into silicon substrate has been studied in Au thin films of various thicknesses (2.0, 5.3, 10.9 and 27.5 nm) deposited on Si(111) and followed by irradiation with 1.5 MeV Au2+ at a flux of 6.3x10^12 ions cm-2 s-1 and fluence up to 1x10^15 ions cm-2. The high resolution transmission electron microscopy measurements showed the presence of gold silicide formation for the above-mentioned systems at fluence greater than equal to 1x1014 ions cm-2. The maximum depth to which the gold atoms have been diffused at a fluence of 1x10^14 ions cm-2 for the cases of 2.0, 5.3, 10.9 and 27.5 nm thick films has been found to be 60, 95, 160 and 13 nm respectively. Interestingly, at higher fluence of 1x1015 ions cm-2 in case of 27.5 nm thick film, gold atoms from the film transported to a maximum depth of 265 nm in the substrate. The substrate silicon is found to be amorphous at the above fluence values where unusually large mass transport occurred. Enhanced diffusion has been explained on the basis of ion beam induced, flux dependent amorphous nature of the substrate, and transient beam induced temperature effects. This work confirms the absence of confinement effects that arise from spatially confined structures and existence of thermal and chemical reactions during ion irradiation.
قيم البحث
اقرأ أيضاً
We report a direct observation of segregation of gold atoms to the near surface regime due to 1.5 MeV Au2+ ion impact on isolated gold nanostructures deposited on silicon. Irradiation at fluences of 6x10^13, 1x10^14 and 5x10^14 ions cm-2 at a high be
am flux of 6.3x1012 ions cm-2 s-1 show a maximum transported distance of gold atoms into the silicon substrate to be 60, 45 and 23 nm, respectively. At a lower fluence (6x1013 ions cm-2) transport has been found to be associated with the formation of gold silicide (Au5Si2). At a high fluence value of 5x10^14 ions cm-2, disassociation of gold silicide and out-diffusion lead to segregation of gold to defect - rich surface and interface region.
We discuss four important aspects of 1.5 MeV Au2+ ion-induced flux dependent sputtering from gold nanostrcutures (of an average size 7.6 nm and height 6.9 nm) that are deposited on silicon substrates: (a) Au sputtering yield at the ion flux of 6.3x10
^12 ions cm-2 s-1 is found to be 312 atoms/ion which is about five times the sputtering yield reported earlier under identical irradiation conditions at a lower beam flux of 10^9 ions cm-2 s-1, (b) the sputtered yield increases with increasing flux at lower fluence and reduces at higher fluence (1.0x10^15 ions cm-2) for nanostructured thin films while the sputtering yield increases with increasing flux and fluence for thick films (27.5 nm Au deposited on Si) (c) Size distribution of sputtered particles has been found to vary with the incident beam flux showing a bimodal distribution at higher flux and (d) the decay exponent obtained from the size distributions of sputtered particles showed an inverse power law dependence ranging from 1.5 to 2.5 as a function of incident beam flux. The exponent values have been compared with existing theoretical models to understand the underlying mechanism. The role of wafer temperature associated with the beam flux has been invoked for a qualitative understanding of the sputtering results in both the nanostructured thin films and thick films.
We report about La0.67Sr0.33MnO3 single crystal manganite thin films in interaction with a gold capping layer. With respect to uncoated manganite layers of the same thickness, Au-capped 4 nm-thick manganite films reveal a dramatic reduction (about 18
5 K) of the Curie temperature TC and a lower saturation low-temperature magnetization M0. A sizeable TC reduction (about 60 K) is observed even when an inert SrTiO3 layer is inserted between the gold film and the 4 nm-thick manganite layer, suggesting that this effect might have an electrostatic origin.
Binary collision simulations of high-fluence 1 keV Si ion implantation into 8 nm thick SiO2 films on (001)Si were combined with kinetic Monte Carlo simulations of Si nanocrystal (NC) formation by phase separation during annealing. For nonvolatile mem
ory applications, these simulations help to control size and location of NCs. For low concentrations of implanted Si, NCs form via nucleation, growth and Ostwald ripening, whereas for high concentrations Si separates by spinodal decomposition. In both regimes, NCs form above a thin NC free oxide layer at the SiO2/Si interface. This, self-adjusted layer has just a thickness appropriate for NC charging by direct electron tunneling. Only in the nucleation regime the width of the tunneling oxide and the mean NC diameter remain constant during a long annealing period. This behavior originates from the competition of Ostwald ripening and Si loss to the Si/SiO2 interface. The process simulations predict that, for nonvolatile memories, the technological demands on NC synthesis are fulfilled best in the nucleation regime.
Investigations of the complex behavior of the magnetization of manganese arsenide thin films due to defects induced by irradiation of slow heavy ions are presented. In addition to the thermal hysteresis suppression already highlighted in M. Trassinel
li et al., Appl. Phys. Lett. 104, 081906 (2014), we report here on new local magnetic features recorded by a magnetic force microscope at different temperatures close to the characteristic sample phase transition. Complementary measurements of the global magnetization measurements in different conditions (applied magnetic field and temperatures) enable to complete the film characterization. The obtained results suggest that the ion bombardment produces regions where the local mechanical constraints are significantly different from the average, promoting the local presence of magneto-structural phases far from the equilibrium. These regions could be responsible for the thermal hysteresis suppression previously reported, irradiation-induced defects acting as seeds in the phase transition.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها