Giant Tuning of Electronic and Thermoelectric Properties by Epitaxial Strain in p-Type Sr-Doped LaCrO3 Transparent Thin Films

83   0   0.0 ( 0 )
 نشر من قبل Romain Bachelet
 تاريخ النشر 2021
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

The impact of epitaxial strain on the structural, electronic, and thermoelectric properties of p-type transparent Sr-doped LaCrO3 thin films has been investigated. For this purpose, high-quality fully strained La0.75Sr0.25CrO3 (LSCO) epitaxial thin films were grown by molecular beam epitaxy on three different (pseudo)cubic (001)-oriented perovskite oxide substrates: LaAlO3, (LaAlO3)0.3(Sr2AlTaO6)0.7, and DyScO3. The lattice mismatch between the LSCO films and the substrates induces in-plane strain ranging from -2.06% (compressive) to +1.75% (tensile). The electric conductivity can be controlled over 2 orders of magnitude, ranging from 0.5 S/cm (tensile strain) to 35 S/cm (compressive strain). Consistently, the Seebeck coefficient S can be finely tuned by a factor of almost 2 from 127 microV/K (compressive strain) to 208 microV/K (tensile strain). Interestingly, we show that the thermoelectric power factor can consequently be tuned by almost 2 orders of magnitude. The compressive strain yields a remarkable enhancement by a factor of 3 for 2% compressive strain with respect to almost relaxed films. These results demonstrate that epitaxial strain is a powerful lever to control the electric properties of LSCO and enhance its thermoelectric properties, which is of high interest for various devices and key applications such as thermal energy harvesters, coolers, transparent conductors, photocatalyzers, and spintronic memories.



قيم البحث

اقرأ أيضاً

We report on the effect of epitaxial strain on magnetic and optical properties of perovskite LaCrO3 (LCO) single crystal thin films. Epitaxial LCO thin films are grown by pulsed laser deposition on proper choice of substrates to impose different stra in states. A combined experimental and theoretical approach is used to demonstrate the direct correlation between lattice-strain and functional properties. The magnetization results show that the lattice anisotropy plays a critical role in controlling the magnetic behavior of LCO films. The strain induced tetragonality in the film lattice strongly affects the optical transitions and charge transfer gap in LCO. This study opens new possibilities to tailoring the functional properties of LCO and related materials by strain engineering in epitaxial growth.
We investigated the crystal and electronic structures of ferroelectric Bi4Ti3O12 (BiT) single crystalline thin films site-specifically substituted with LaCoO3 (LCO). The epitaxial films were grown by pulsed laser epitaxy on NdGaO3 and SrTiO3 substrat es to vary the degree of strain. With increasing the LCO substitution, we observed a systematic increase in the c-axis lattice constant of the Aurivillius phase related with the modification of pseudo-orthorhombic unit cells. These compositional and structural changes resulted in a systematic decrease in the band gap, i.e., the optical transition energy between the oxygen 2p and transition metal 3d states, based on a spectroscopic ellipsometry study. In particular, the Co 3d state seems to largely overlap with the Ti t2g state, decreasing the band gap. Interestingly, the applied tensile strain facilitates the band gap narrowing, demonstrating that epitaxial strain is a useful tool to tune the electronic structure of ferroelectric transition metal oxides.
The interrelation between the epitaxial strain and oxygen deficiency in La0.7Ca0.3MnO3-{delta} thin films was studied in terms of structural and functional properties. The films with a thickness of 1000{AA} were prepared using a PLD system equipped w ith a RHEED facility and a pyrometric film temperature control. The epitaxial strain and the oxygen deficiency in the samples were systematically modified using three different substrates: SrTiO3, (LaAlO3)0.3-(Sr2AlTaO6)0.7 and LaSrAlO4, and four different oxygen pressures during film growth ranging from 0.27mbar to 0.1mbar. It could be demonstrated that the oxygen incorporation depends on the epitaxial strain: oxygen vacancies were induced to accommodate tensile strain whereas the compressive strain suppressed the generation of oxygen vacancies.
We report a giant resistance drop induced by dc electrical currents in La0.67Ca0.33MnO3 epitaxial thin films. Resistance of the patterned thin films decreases exponentially with increasing current and a maximum drop shows at the temperature of resist ance peak Tp. Variation of resistance with current densities can be scaled below and above Tp, respectively. This work can be useful for the future applications of electroresistance.
The double perovskite Sr2CrReO6 is an interesting material for spintronics, showing ferrimagnetism up to 635 K with a predicted high spin polarization of about 86%. We fabricated Sr2CrReO6 epitaxial films by pulsed laser deposition on (001)-oriented SrTiO3 substrates. Phase-pure films with optimum crystallographic and magnetic properties were obtained by growing at a substrate temperature of 700 degree C in pure O2 of 6.6x10-4 mbar. The films are c-axis oriented, coherently strained, and show less than 20% anti-site defects. The magnetization curves reveal high saturation magnetization of 0.8 muB per formula unit and high coercivity of 1.1 T, as well as a strong magnetic anisotropy.