We have investigated the substitution effect of Eu on the superconductivity in La2-xEuxO2Bi3Ag0.6Sn0.4S6. Recently, we reported an observation of superconductivity at 0.5 K in a layered oxychalcogenide La2O2Bi3AgS6. The Sn doping at the Ag site was found to raise the superconducting transition temperature, Tc to 2.5 K in La2O2Bi3Ag0.6Sn0.4S6. To further improve the superconducting properties, we have partially substituted Eu for the La site to increase the chemical pressure in La2-xEuxO2Bi3Ag0.6Sn0.4S6 (x = 0.1 to 0.6). With the increase in Eu concentration, x, the lattice constant a was found to shrink, while the lattice constant c was marginally shortened, which suggests that the chemical pressure induced by the Eu doping is uniaxial along the a-axis. Tc was observed to increase with increasing x up to x = 0.4, further decreasing for higher Eu concentrations of x = 0.5 and 0.6. From the magnetic susceptibility and resistivity measurements, the bulk nature of superconductivity has been observed for x = 0.1 to 0.5 with Tc = 2.5 to 4.0 K, respectively. The upper critical field (Bc2) was noted to be 3.5 T for x = 0.4, which also has the highest Tc.
قيم البحث
اقرأ أيضاً
A series of high-quality under-doped La2-xSrxCuO4 superconductor crystals with x = 0.063 - 0.125 were prepared by traveling-solvent floating-zone (TSFZ) technique. We found by dc magnetic measurements that, in this series of crystals, the superconduc
ting transition was quite sharp in the vicinity of the hole densities of x = 1/16 and x = 1/9 while it was much broader away from these two magic numbers, and the Meissner fraction showed a remarkable minimum near x = 1/9. We concluded that these phenomena are reflections of intrinsic properties of this cuprate system. Our observations are discussed in light of recently proposed composite charge model together with charge inhomogeneity and electronic phase separations.
Among iron 122 pnictide superconductors, the EuFe$_2$As$_2$ series draws particular interest because, in addition to superconductivity or the long-range spin-density-wave order in the Fe subsystem, the localized Eu$^{2+}$ magnetic moments order at lo
w temperatures. Here we present a novel scheme of how the spins align in the Eu compounds when pressure varies the coupling; we explain magnetization measurements on EuFe$_2$(As$_{1-x}$P$_x$)$_2$ single crystals as well as other observations of the Eu$^{2+}$ ordering previously reported in literature. The magnetic moments of the Eu$^{2+}$ ions are slightly canted even in the parent compound EuFe$_2$As$_2$, yielding a ferromagnetic contribution along the $c$-direction that becomes stronger with pressure. Reducing the interlayer distance even further, the antiferromagnetic coupling of the $ab$ planes finally turns ferromagnetic.
Ru{1-x}Sn{x}Sr2EuCu2O8 and Ru{1-x}Sn{x}Sr2GdCu2O8 have been comprehensively studied by microwave and dc resistivity and magnetoresistivity and by the dc Hall measurements. The magnetic ordering temperature T_m is considerably reduced with increasing
Sn content. However, doping with Sn leads to only slight reduction of the superconducting critical temperature T_c accompanied with the increase of the upper critical field B_c2, indicating an increased disorder in the system and a reduced scattering length of the conducting holes in CuO2 layers. In spite of the increased scattering rate, the normal state resistivity and the Hall resistivity are reduced with respect to the pure compound, due to the increased number of itinerant holes in CuO2 layers, which represent the main conductivity channel. Most of the electrons in RuO2 layers are presumably localized, but the observed negative magnetoresistance and the extraordinary Hall effect lead to the conclusion that there exists a small number of itinerant electrons in RuO$_2$ layers that exhibit colossal magnetoresistance.
We investigated the influence of different Ag additions (up to 10 wt %) on the superconducting properties of FeSe0.94. The structural investigations (XRD and SEM) indicated that Ag is present in three different forms. Ag at grain boundaries supports
the excellent intergrain connections and reduces superconducting transition width to values smaller than 1K at B=0 and smaller than 2.74 K at B=14 T. Ag insertion in the crystal lattice unit cell provides additional carriers and changes the electron hole imbalance in FeSe0.94. This results in an increase in the magnetoresistive effect (MR) and critical temperature (Tc). Reacted Ag forms a small amount (~1%) of Ag2Se impurity phase, which may increase the pinning energy in comparison with that of the undoped sample. The enhanced upper critical field (Bc2) is also a result of the increased impurity scattering. Thus, unlike cuprates Ag addition enhances the Tc, Bc2, pinning energy and MR making the properties of polycrystalline FeSe0.94 similar to those of single crystals.
Resistivity and magnetic susceptibility measurements under external pressure were performed on single-crystals NaFe1-xCoxAs (x=0, 0.01, 0.028, 0.075, 0.109). The maximum Tc enhanced by pressure in both underdoped and optimally doped NaFe1-xCoxAs is t
he same, as high as 31 K. The overdoped sample with x = 0.075 also shows a positive pressure effect on Tc, and an enhancement of Tc by 13 K is achieved under pressure of 2.3 GPa. All the superconducting samples show large positive pressure coefficient on superconductivity, being different from Ba(Fe1-xCox)2As2. However, the superconductivity cannot be induced by pressure in heavily overdoped non-superconducting NaFe0.891Co0.109As. These results provide evidence for that the electronic structure is much different between superconducting and heavily overdoped non-superconducting NaFe1-xCoxAs, being consistent with the observation by angle-resolved photoemission spectroscopy.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها