تسجيل مستخدم جديدStructural, magnetic, and electrical properties of collinear antiferromagnetic heteroepitaxy cubic Mn$_3$Ga thin films
272
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Although a cubic phase of Mn$_3$Ga with an antiferromagnetic order has been theoretically predicted, it has not been experimentally verified in a bulk or film form. Here, we report the structural, magnetic, and electrical properties of antiferromagnetic cubic Mn$_3$Ga (C-Mn$_3$Ga) thin films, in comparison with ferrimagnetic tetragonal Mn$_3$Ga (T-Mn3Ga). The structural analyses reveal that C-Mn$_3$Ga is hetero-epitaxially grown on MgO substrate with the Cu$_3$Au-type cubic structure, which transforms to T-Mn$_3$Ga as the RF sputtering power increases. The magnetic and magnetotransport data show the antiferromagnetic transition at T$_N$ = 400 K for C-Mn$_3$Ga and the ferrimagnetic transition at T$_C$ = 820 K for T-Mn$_3$Ga. Furthermore, we find that the antiferromagnetic C-Mn$_3$Ga exhibits a higher electrical resistivity than the ferrimagnetic T-Mn$_3$Ga, which can be understood by spin-dependent scattering mechanism.
قيم البحث
اقرأ أيضاً
We investigated structural, magnetic and electrical properties of sputter deposited Mn-Fe-Ga compounds. The crystallinity of the Mn-Fe-Ga thin films was confirmed using x-ray diffraction. X-ray reflection and atomic force microscopy measurements were
utilized to investigate the surface properties, roughness, thickness and density of the deposited Mn-Fe-Ga. Depending on the stoichiometry, as well as the used substrates (SrTiO3 (001) and MgO (001)) or buffer layer (TiN) the Mn-Fe-Ga crystallizes in the cubic or the tetragonally distorted phase. Anomalous Hall effect and alternating gradient magnetometry measurements confirmed strong perpendicular magnetocrystalline anisotropy. Low saturation magnetization and hard magnetic behavior was reached by tuning the composition. Temperature dependent anomalous Hall effect measurements in a closed cycle He-cryostat showed a slight increase in coercivity with decreasing temperature (300K to 2K). TiN buffered Mn2.7Fe0.3Ga revealed sharper switching of the magnetization compared to the unbuffered layers.
We report the optical, electrical, and structural properties of Si doped $beta$-Ga$_2$O$_3$ films grown on (010)-oriented $beta$-Ga$_2$O$_3$ substrate via HVPE. Our results show that, despite growth rates that are more than one order of magnitude fas
ter than MOCVD, films with mobility values of up to 95 cm$^2$V$^{-1}$s$^{-1}$ at a carrier concentration of 1.3$times$10$^{17}$ cm$^{-3}$ can be achieved using this technique, with all Si-doped samples showing n-type behavior with carrier concentrations in the range of 10$^{17}$ to 10$^{19}$ cm$^{-3}$. All samples showed similar room temperature photoluminescence, with only the samples with the lowest carrier concentration showing the presence of a blue luminescence, and the Raman spectra exhibiting only phonon modes that belong to $beta$-Ga$_2$O$_3$, indicating that the Ga$_2$O$_3$ films are phase pure and of high crystal quality. We further evaluated the epitaxial quality of the films by carrying out grazing incidence X-ray scattering measurements, which allowed us to discriminate the bulk and film contributions. Finally, MOS capacitors were fabricated using ALD HfO$_2$ to perform C-V measurements. The carrier concentration and dielectric values extracted from the C-V characteristics are in good agreement with Hall probe measurements. These results indicate that HVPE has a strong potential to yield device-quality $beta$-Ga$_2$O$_3$ films that can be utilized to develop vertical devices for high-power electronics applications.
Antiferromagnetic materials are of great interest for spintronics. Here we present a comprehensive study of the growth, structural characterization, and resulting magnetic properties of thin films of the non-collinear antiferromagnet Mn$_{3}$Ir. Usin
g epitaxial engineering on MgO (001) and Al$_{2}$O$_{3}$ (0001) single crystal substrates, we control the growth of cubic ${gamma}$-Mn$_{3}$Ir in both (001) and (111) crystal orientations, and discuss the optimization of growth conditions to achieve high-quality crystal structures with low surface roughness. Exchange bias is studied in bilayers, with exchange bias fields as large as -29 mT (equivalent to a unidirectional anisotropy constant of 11.5 nJ cm$^{-2}$) measured in Mn$_{3}$Ir (111) / permalloy heterostructures at room temperature. In addition, a distinct dependence of blocking temperature on in-plane crystallographic direction in Mn$_{3}$Ir (001) / Py bilayers is observed. These findings are discussed in the context of chiral antiferromagnetic domain structures, and will inform progress towards topological antiferromagnetic spintronic devices.
We investigated the structural and magnetic properties of bare SrRuO$_3$ (SRO) ultra-thin films and SrRuO$_3$/SrIrO$_3$/SrZrO$_3$ (SRO/SIO/SZO: RIZ) trilayer heterostructures between 10 K and 80 K, by comparing macroscopic data using magneto-optical
Kerr effect (MOKE) and magneto-transport (anomalous Hall effect: AHE), with nanoscale fingerprints when applying non-contact scanning force microscopy (nc-SFM) and magnetic force microscopy (MFM). SRO and RIZ ultra-thin films were epitaxially grown at 650C onto vicinal SrTiO$_3$ (100) single-crystalline substrates to a nominal thickness of 4 and 4/2/2 unit cells (uc), respectively. Our correlated analysis allows associating topographic sample features of overgrown individual layers to their residual magnetization, as is shown here to be relevant for interpreting the macroscopic AHE data. Although the hump-like features in the AHE suggest a magnetically extured skyrmion phase to exist around 55 K associated to the topological Hall effect (THE), both our MOKE and MFM data cannot support this theory. In contrast, our SFM/MFM local-scale analysis finds the local coercive field to be strongly dependent on the effective layer thickness and stoichiometry in both the SRO and RIZ samples, with huge impact on the local band-structure. In fact, it is these variations that in turn mimic a potential THE through anomalies in the AHE resistivity loops.
The composition dependence of the structural, magnetic, and transport properties of epitaxially grown Mn-Co-Ga films were investigated. The crystal structure was observed to change from tetragonal to cubic as the Co content was increased. In terms of
the dependence of saturation magnetization on the Co content, relatively small value was obtained for the Mn$_{2.3}$Co$_{0.4}$Ga$_{1.3}$ film at a large {it K}$_textrm u$ value of 9.2 Merg/cm$^3$. Electrical resistivity of Mn-Co-Ga films was larger than that of pure Mn-Ga film. The maximum value of the resistivity was 490 $muOmega$cm for Mn$_{2.2}$Co$_{0.6}$Ga$_{1.2}$ film. The high resistivity of Mn-Co-Ga might be due to the presence of localized electron states in the films due to chemical disordering caused by the Co substitution.