We report the temperature-pressure-magnetic field phase diagram made from electrical resistivity measurements for the ferromagnetic (FM) Kondo lattice CeRuPO. The ground state at zero field changes from the FM state to another state, which is suggested to be an antiferromagnetic (AFM) state, above ~0.7 GPa, and the magnetically ordered state is completely suppressed at ~2.8 GPa. In addition to the collapse of the AFM state under pressure and a magnetic field, a metamagnetic (MM) transition from a paramagnetic state to a polarized paramagnetic state appears. CeRuPO will give us a rich playground for understanding the mechanism of the MM transition under comparable FM and AFM correlations in the Kondo lattice.
قيم البحث
اقرأ أيضاً
We have determined the physical ground state properties of the compounds CeRuPO and CeOsPO by means of magnetic susceptibility chi(T), specific heat C(T), electrical resistivity rho(T), and thermopower S(T) measurements. chi(T) reveals a trivalent 4f
1 cerium state in both compounds. For CeRuPO a pronounced decrease of rho(T) below 50K indicates the onset of coherent Kondo scattering which is confirmed by enhanced S(T). The temperature and magnetic field dependence of chi(T) and C(T) evidence ferromagnetic (FM) order at TC=15K. Thus, CeRuPO seems to be one of the rare example of a FM Kondo lattice. In contrast, CeOsPO shows antiferromagnetic order at TN=4.4K despite only minor changes in lattice parameters and electronic configuration. Additional 31P NMR results support these scenarios. LSDA+U calculations evidence a quasi two dimensional electronic band structure, reflecting a strong covalent bonding within the CeO and RuP layers and a weak ionic like bonding between the layers.
The magnetic ground state phase diagram of the ferromagnetic Kondo-lattice model is constructed by calculating internal energies of all possible bipartite magnetic configurations of the simple cubic lattice explicitly. This is done in one dimension (
1D), 2D and 3D for a local moment of S = 3/2. By assuming saturation in the local moment system we are able to treat all appearing higher local correlation functions within an equation of motion approach exactly. A simple explanation for the obtained phase diagram in terms of bandwidth reduction is given. Regions of phase separation are determined from the internal energy curves by an explicit Maxwell construction.
We report the temperature-pressure-magnetic field phase diagram of the ferromagnetic Kondo-lattice CeTiGe$_3$ determined by means of electrical resistivity measurements. Measurements up to $sim$ 5.8 GPa reveal a rich phase diagram with multiple phase
transitions. At ambient pressure, CeTiGe$_3$ orders ferromagnetically at $T_text{C}$ = 14 K. Application of pressure suppresses $T_text{C}$, but a pressure induced ferromagnetic quantum criticality is avoided by the appearance of two new successive transitions for $p$ $>$ 4.1 GPa that are probably antiferromagnetic in nature. These two transitions are suppressed under pressure, with the lower temperature phase being fully suppressed above 5.3 GPa. The critical pressures for the presumed quantum phase transitions are $p_1$ $cong$ 4.1 GPa and $p_2$ $cong$ 5.3 GPa. Above 4.1 GPa, application of magnetic field shows a tricritical point evolving into a wing structure phase with a quantum tricritical point at 2.8 T at 5.4 GPa, where the first order antiferromagnetic-ferromagnetic transition changes into the second order antiferromagnetic-ferromagnetic transition.
We measured the thermal expansion of the valence fluctuating phase of SmS (golden SmS) to construct a pressure vs temperature phase diagram. The obtained phase diagram is characterized by three lines. One is a crossover line that divides the paramagn
etic phase into two regions. The other two lines correspond to a second-order Neel transition and a first-order Neel transition. The crossover line appears to emerge from a tricritical point that separates the first-order Neel transition from the second-order one. We argue that a valence jump occurs at the border of antiferromagnetism.
Electrical resistivity and ac-susceptibility measurements under high pressure were carried out in high-quality single crystals of $alpha$-Mn. The pressure-temperature phase diagram consists of an antiferromagnetic ordered phase (0<$P$<1.4 GPa, $T<T_{
rm N}$), a pressure-induced ordered phase (1.4<$P$<4.2-4.4 GPa, $T<T_{rm A}$), and a paramagnetic phase. A significant increase was observed in the temperature dependence of ac-susceptibility at $T_{rm A}$, indicating that the pressure-induced ordered phase has a spontaneous magnetic moment. Ferrimagnetic order and parasitic ferromagnetism are proposed as candidates for a possible magnetic structure. At the critical pressure, where the pressure-induced ordered phase disappears, the temperature dependence of the resistivity below 10 K is proportional to $T^{5/3}$. This non-Fermi liquid behavior suggests the presence of pronounced magnetic fluctuation.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها