Electric-field-induced resistance switching (RS) phenomena have been studied for over 60 years in metal/dielectrics/metal structures. In these experiments a wide range of dielectrics have been studied including binary transition metal oxides, perovskite oxides, chalcogenides, carbon- and silicon-based materials, as well as organic materials. RS phenomena can be used to store information and offer an attractive performance, which encompasses fast switching speeds, high scalability, and the desirable compatibility with Si-based complementary-metal-oxide-semiconductor fabrication. This is promising for nonvolatile memory technology, i.e. resistance random access memory (RRAM). However, a comprehensive understanding of the underlying mechanism is still lacking. This impedes a faster product development as well as an accurate assessment of the device performance potential. Generally speaking, RS occurs not in the entire dielectric but only a small, confined region, which results from the local variation of conductivity in dielectrics. In this review, we focus on the RS in oxides with such an inhomogeneous conductivity. According to the origin of the conductivity inhomogeneity, the RS phenomena and their working mechanism are reviewed by dividing them into two aspects: interface RS, based on the change of contact resistance at metal/oxide interface due to the change of Schottky barrier and interface chemical layer, and bulk RS, realized by the formation, connection, and disconnection of conductive channels in the oxides. Finally the current challenges of RS investigation and the potential improvement of the RS performance for the nonvolatile memories are discussed.
قيم البحث
اقرأ أيضاً
The weak temperature dependence of the resistance R(T) of monolayer graphene1-3 indicates an extraordinarily high intrinsic mobility of the charge carriers. Important complications are the presence of mobile scattering centres that strongly modify ch
arge transport, and the presence of strong mesoscopic conductance fluctuations that, in graphene, persist to relatively high temperatures4,5. In this Letter, we investigate the surprisingly varied changes in resistance that we find in graphene flakes as temperature is lowered below 70 K. We propose that these changes in R(T) arise from the temperature dependence of the scattered electron wave interference that causes the resistance fluctuations. Using the field effect transistor configuration, we verify this explanation in detail from measurements of R(T) by tuning to different gate voltages corresponding to particular features of the resistance fluctuations. We propose simple expressions that model R(T) at both low and high charge carrier densities.
Thermal switching provides an effective way for active heat flow control, which has recently attracted increasing attention in terms of nanoscale thermal management technologies. In magnetic and spintronic materials, the thermal conductivity depends
on the magnetization configuration: this is the magneto-thermal resistance effect. Here we show that an epitaxial Cu/Co$_{50}$Fe$_{50}$ multilayer film exhibits giant magnetic-field-induced modulation of the cross-plane thermal conductivity. The magneto-thermal resistance ratio for the Cu/Co$_{50}$Fe$_{50}$ multilayer reaches 150% at room temperature, which is much larger than the previous record high. Although the ratio decreases with increasing the temperature, the giant magneto-thermal resistance effect of ~100% still appears up to 400 K. The magnetic field dependence of the thermal conductivity of the Cu/Co$_{50}$Fe$_{50}$ multilayer was observed to be about twice greater than that of the cross-plane electrical conductivity. The observation of the giant magneto-thermal resistance effect clarifies a potential of spintronic multilayers as thermal switching devices.
We present a theoretical proposal for the design of a thermal switch based on the anisotropy of the thermal conductivity of PbTiO3 and of the possibility to rotate the ferroelectric polarization with an external electric field. Our calculations are b
ased on an iterative solution of the phonon Boltzmann Transport Equation and rely on interatomic force constants computed within an efficient second-principles density functional theory scheme. We also characterize the hysteresis cycle of the thermal conductivity in presence of an applied electric field and show that the response time would be limited by speed of the ferroelectric switch itself and thus can operate in the high-frequency regime.
We fabricated Pt/NiO/Pt capacitor structures with various bottom electrode thicknesses, $t_{BE}$, and investigated their resistance switching behaviors. The capacitors with $t_{BE} geq 50$ nm exhibited typical unipolar resistance memory switching, wh
ile those with $t_{BE} leq 30$ nm showed threshold switching. This interesting phenomenon can be explained in terms of the temperature-dependent stability of conducting filaments. In particular, the thinner $t_{BE}$ makes dissipation of Joule heat less efficient, so the filaments will be at a higher temperature and become less stable. This study demonstrates the importance of heat dissipation in resistance random access memory.
While the recent establishment of the role of thermophoresis/diffusion-driven oxygen migration during resistance switching in metal oxide memristors provided critical insights required for memristor modeling, extended investigations of the role of ox
ygen migration during ageing and failure remain to be detailed. Such detailing will enable failure-tolerant design, which can lead to enhanced performance of memristor-based next-generation storage-class memory. Here we directly observed lateral oxygen migration using in-situ synchrotron x-ray absorption spectromicroscopy of HfOx memristors during initial resistance switching, wear over millions of switching cycles, and eventual failure, through which we determined potential physical causes of failure. Using this information, we reengineered devices to mitigate three failure mechanisms, and demonstrated an improvement in endurance of about three orders of magnitude.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها