Triblock terpolymers exhibit a rich self-organization behavior including the formation of fascinating cylindrical core-shell structures with a phase separated corona. After crystallization-induced self-assembly of polystryrene-(block)-polyethylene-(block)-poly(methyl methacrylate) triblock terpolymers (abbreviated as SEMs = Styrene-Ethylene-Methacrylates) from solution, worm-like core-shell micelles with a patchy corona of polystryrene and poly(methyl methacrylate) were observed by transmission electron microscopy. However, the solution structure is still a matter of debate. Here, we present a method to distinguish in-situ between a Janus-type (two faced) and a patchy (multiple compartments) configuration of the corona. To discriminate between both models the scattering intensity must be determined mainly by one corona compartment. Contrast variation in small-angle neutron scattering enables us to focus on one compartment of the SEMs. The results validate the existence of the patchy structure also in solution.
قيم البحث
اقرأ أيضاً
Small-angle neutron scattering (SANS) from cationic globular micellar solutions composed of sodium dodecyl sulfate (SDS) and in water was studied with contrast variation approach. Extensive computational studies have demonstrated that the distributio
n of invasive water is clearly an important feature for understanding the self-organization of SDS molecules and the stability of assemblies. However, in existing scattering studies the degree of hydration level was not examined explicitly. Here using the scheme of contrast variation, we establish a methodology of SANS to determine the intra-micellar radial dis-tributions of invasive water and SDS molecules from the evolving spectral lineshapes caused by the varying isotopic ratio of water. A detailed description hydration of SDS micelles is provided, which in an excellent agreement with known results of many existing simulations studies. Extension of our method can be used to provide an in-depth insight into the micellization phenomenon which is commonly found in many soft matter systems.
We report Small-Angle Neutron Scattering (SANS) measurements on the vortex lattice in a PbIn polycrystal in the presence of an applied current. Using the rocking curves as a probe of the distribution of current in the sample, we observe that vortex p
inning is due to the surface roughness. This leads to a surface current that persists in the flux flow region. We show the influence of surface treatments on the distribution of this current.
Flux Lines Lattice (FLL) states have been studied using transport measurements and Small Angle Neutron Scattering in low T$_c$ materials. In Pb-In, the bulk dislocations in the FLL do not influence the transport properties. In Fe doped NbSe$_{2}$, tr
ansport properties can differ after a Field Cooling (FC) or a Zero Field Cooling (ZFC) procedure, as previously reported. The ZFC FLL is found ordered with narrow Bragg Peaks and is linked to a linear V(I) curve and to a superficial critical current. The FC FLL pattern exhibits two Bragg peaks and the corresponding V(I) curve shows a S-shape. This can be explained by the coexistence of two ordered FLL slightly tilted from the applied field direction by different superficial currents. These currents are wiped out when the transport current is increased.
We have evidenced by small angle neutron scattering at low temperature the coexistence of ferromagnetism (F) and antiferromagnetism (AF) in Pr0.67Ca0.33MnO3. The results are compared to those obtained in Pr0.80Ca0.20MnO3 and Pr0.63Ca0.37MnO3, which a
re F and AF respectively. Quantitative analysis shows that the small angle scattering is not due to a mesoscopic mixing but to a nanoscopic electronic and magnetic red cabbage structure, in which the ferromagnetic phase exists in form of thin layers in the AF matrix (stripes or 2D sheets).
We have observed a magnetic vortex lattice (VL) in BaFe2(As_{0.67}P_{0.33})2 (BFAP) single crystals by small-angle neutron scattering (SANS). With the field along the c-axis, a nearly isotropic hexagonal VL was formed in the field range from 1 to 16
T, which is a record for this technique in the pnictides, and no symmetry changes in the VL were observed. The temperature-dependence of the VL signal was measured and confirms the presence of (non d-wave) nodes in the superconducting gap structure for measurements at 5 T and below. The nodal effects were suppressed at high fields. At low fields, a VL reorientation transition was observed between 1 T and 3 T, with the VL orientation changing by 45{deg}. Below 1 T, the VL structure was strongly affected by pinning and the diffraction pattern had a fourfold symmetry. We suggest that this (and possibly also the VL reorientation) is due to pinning to defects aligned with the crystal structure, rather than being intrinsic.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها