We have developed disk-shaped MgB2 bulk superconducting magnets (20, 30 mm in diameter, 10 mm in thickness) using the in-situ process from Mg and B powders and evaluated the temperature dependence of trapped magnetic field. A pair of two disc-shaped bulks of 30 mm in diameter and 10 mm in thickness magnetized by field-cooling condition showed trapped fields of 1.2, 2.8 and 3.1 T at 30, 20 and 17.5 K, respectively. High trapped field over 3 T was recorded for the first time.
قيم البحث
اقرأ أيضاً
Superconductors with persistent zero-resistance currents serve as permanent magnets for high-field applications requiring a strong and stable magnetic field, such as magnetic resonance imaging (MRI). The recent global helium shortage has quickened re
search into high-temperature superconductors (HTSs) materials that can be used without conventional liquid-helium cooling to 4.2 K. Herein, we demonstrate that 40-K-class metallic HTS magnesium diboride (MgB2) makes an excellent permanent bulk magnet, maintaining 3 T at 20 K for 1 week with an extremely high stability (<0.1 ppm/h). The magnetic field trapped in this magnet is uniformly distributed, as for single-crystalline neodymium-iron-boron. Magnetic hysteresis loop of the MgB2 permanent bulk magnet was detrmined. Because MgB2 is a simple-binary-line compound that does not contain rare-earth metals, polycrystalline bulk material can be industrially fabricated at low cost and with high yield to serve as strong magnets that are compatible with conventional compact cryocoolers, making MgB2 bulks promising for the next generation of Tesla-class permanent-magnet applications.
We report the effect of adipic acid (C6H10O4) doping on lattice parameters, microstructure, critical temperature (Tc), current density (Jc), and irreversibility field (Hirr) for MgB2 superconductor. Actual carbon (C) substitution level for boron (B)
is estimated to be from 0.40 percent to 2.95 percent for different doping levels. A reduction in Tc from 38.43 to 34.93 K and in lattice parameter a from 3.084(3) A to 3.075(6) Ais observed for the10 wt percent C6H10O4 doped sample in comparison to pristine MgB2. This is an indication of C substitution at boron sites, with the C coming from the decomposition of C6H10O4 at the time of reaction. Interestingly the doped samples have resulted in significant enhancement of Jc and Hirr. All the doped samples exhibit the Jc value of the order of 10^4 A/cm2 at 5 K and 8 T, which is higher by an order of magnitude as compared to undoped sample. This result indicates that C6H10O4 is a promising material for MgB2 for obtaining the excellent Jc values under higher magnetic fields.
High quality bulk MgB2 exhibit a structure of voids and agglomeration of crystals on different length-scales. Because of this, the superconducting currents percolate between the voids in the ensuing structure. Magnetic measurements reveal that the su
perconducting currents circulate on at least three different length-scales, of ~1 micrometre, ~10 micrometre and whole of the sample (~millimetre). Each of these screenings contributes to the measured irreversible magnetic moment (Dm). The analysis of the field dependence of Dm for samples of subsequently decreasing size showed that the critical current obtained using the simple critical state model is erroneous. This leads to the artefact of the sample size-dependent critical current and irreversibility field. Our data analysis enables the separation of the contribution of each of the screening currents to Dm. The field dependence of each of the currents follows a stretched exponential form. The currents flowing around whole of the sample give a dominant contribution to Dm in the intermediate fields (1T < H < 4T at 20K) and they can be used to obtain the value of Jc from critical state model, which corresponds to the transport Jc.
Sintered samples of MgB2 were irradiated in a fission reactor. Defects in the bulk microstructure are produced during this process mainly by the 10B(n,a)7Li reaction while collisions of fast neutrons with the lattice atoms induce much less damage. Se
lf-shielding effects turn out to be very important and lead to a highly inhomogeneous defect distribution in the irradiated samples. The resulting disorder enhances the normal state resistivity and the upper critical field. The irreversibility line shifts to higher fields at low temperatures and the measured critical current densities increase following irradiation.
We study the effect of synthesis temperature on the phase formation in nano(n)-SiC added bulk MgB2 superconductor. In particular we study: lattice parameters, amount of carbon (C) substitution, microstructure, critical temperature (Tc), irreversibili
ty field (Hirr), critical current density (Jc), upper critical field (Hc2) and flux pinning. Samples of MgB2+(n-SiC)x with x=0.0, 0.05 & 0.10 were prepared at four different synthesis temperatures i.e. 850, 800, 750, and 700oC with the same heating rate as 10oC/min. We found 750oC as the optimal synthesis temperature for n-SiC doping in bulk MgB2 in order to get the best superconducting performance in terms of Jc, Hc2 and Hirr. Carbon (C) substitution enhances the Hc2 while the low temperature synthesis is responsible for the improvement in Jc due to the smaller grain size, defects and nano-inclusion induced by C incorporation into MgB2 matrix, which is corroborated by elaborative HRTEM (high-resolution transmission electron microscopy) results. We optimized the the Tc(R=0) of above 15K for the studied n-SiC doped and 750 0C synthesized MgB2 under 140 KOe field, which is one of the highest values yet obtained for variously processed and nano-particle added MgB2 in literature to our knowledge.