تسجيل مستخدم جديدStudy of surface-bulk mass transport and phase transformation in nano TiO2 using hyperfine interaction technique
76
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
Phase transition from anatase to rutile for the 70nm TiO2 crystallite has been investigated by annealing at different temperatures followed by TDPAC measurement of these TiO2 crystallites adsorbed with 181Hf tracer. The width of the peaks in XRD spectra for TiO2 crystallites annealed at different temperatures indicates the growth of the crystallites with temperature. The samples annealed upto 823K for 4hrs showed no phase transition, except the growth of the crystallites. However, it showed phase transition at the same temperature (823K), when annealed for longer duration. Annealing for shorter duration at 1123K showed phase transition. 181Hf tracer adsorbed on 70 nm anatase TiO2 is found to be in different polymorphs (anatase & rutile) formed during annealing process. Surface to bulk mass-transfer is found to play a significant role in the phase transition process.
قيم البحث
اقرأ أيضاً
The nuclear quadrupole interaction of the I=5/2 state of the nuclear probes 111Cd and 181Ta in the anatase and rutile polymorphs of bulk TiO2 was studied using the time differential perturbed angular correlation (TDPAC). The fast-slow coincidence set
up is based on the CAMAC electronics. For anatase, the asymmetry of the electric field gradient was eta=0.22(1) and a quadrupole interaction frequency: 44.01(3) Mrad/s was obtained for 181Ta. For rutile, the respective values are eta=0.56(1) and quadrupole frequency=130.07(9) Mrad/s. The values for rutile match closely with the literature values. In case of the 111Cd probe produced from the beta decay of 111Ag, the quadrupole interaction frequency and the asymmetry parameter for anatase was negligible. This indicates an unperturbed angular correlation in anatase. On the other hand for rutile, the quadrupole frequency is 61.74(2) Mrad/s and the asymmetry is 0.23(1) for 111Cd probe. The results have been interpreted in terms of the surrounding atom positions in the lattice and the charge state of the probe nucleus.
A series of nine samples of sigma-Fe_{100-x}Mo_x with 44<x<57 were synthesized by a sintering method. The samples were investigated experimentally and theoretically. Using X-ray diffraction techniques structural parameters such as lattice constants,
atomic positions within the unit cell and populations of atoms over five different sublattices were determined. An information on charge-densities and electric field gradients at particular lattice sites was obtained by application of the Korringa-Kohn-Rostoker (KKR) method for electronic structure calculations. Hyperfine quantities calculated with KKR were successfully applied to analyze Mossbauer spectra measured at room temperature.
Ab-initio density functional theory (DFT) calculations of the relative stability of anatase and rutile polymorphs of TiO2 were carried using all-electron atomic orbitals methods with local density approximation (LDA). The rutile phase exhibited a mod
erate margin of stability of ~ 3 meV relative to the anatase phase in pristine material. From computational analysis of the formation energies of Si, Al, Fe and F dopants of various charge states across different Fermi level energies in anatase and in rutile, it was found that the cationic dopants are most stable in Ti substitutional lattice positions while formation energy is minimised for F- doping in interstitial positions. All dopants were found to considerably stabilise anatase relative to the rutile phase, suggesting the anatase to rutile phase transformation is inhibited in such systems with the dopants ranked F>Si>Fe>Al in order of anatase stabilisation strength. Al and Fe dopants were found to act as shallow acceptors with charge compensation achieved through the formation of mobile carriers rather than the formation of anion vacancies.
Many Prussian Blue Analogues are known to show a thermally induced phase transition close to room temperature and a reversible, photo-induced phase transition at low temperatures. This work reports on magnetic measurements, X-ray photoemission and Ra
man spectroscopy on a particular class of these molecular heterobimetallic systems, specifically on Rb0.81Mn[Fe(CN)6]0.95_1.24H2O, Rb0.97Mn[Fe(CN)6]0.98_1.03H2O and Rb0.70Cu0.22Mn0.78[Fe(CN)6]0.86_2.05H2O, to investigate these transition phenomena both in the bulk of the material and at the sample surface. Results indicate a high degree of charge transfer in the bulk, while a substantially reduced conversion is found at the sample surface, even in case of a near perfect (Rb:Mn:Fe=1:1:1) stoichiometry. Thus, the intrinsic incompleteness of the charge transfer transition in these materials is found to be primarily due to surface reconstruction. Substitution of a large fraction of charge transfer active Mn ions by charge transfer inactive Cu ions leads to a proportional conversion reduction with respect to the maximum conversion that is still stoichiometrically possible and shows the charge transfer capability of metal centers to be quite robust upon inclusion of a neighboring impurity. Additionally, a 532 nm photo-induced metastable state, reminiscent of the high temperature Fe(III)Mn(II) ground state, is found at temperatures 50-100 K. The efficiency of photo-excitation to the metastable state is found to be maximized around 90 K. The photo-induced state is observed to relax to the low temperature Fe(II)Mn(III) ground state at a temperature of approximately 123 K.
Contrary to previous studies that identified the ground state crystal structure of the entire R_3Co series (R is a rare earth) as orthorhombic Pnma, we show that Y_3Co undergoes a structural phase transition at T_t=160K. Single crystal neutron diffra
ction data reveal that at T_t the trigonal prisms formed by a cobalt atom and its six nearest-neighbor yttrium atoms experience distortions accompanied by notable changes of the Y-Co distances. The formation of the low-temperature phase is accompanied by a pronounced lattice distortion and anomalies seen in heat capacity and resistivity measurements. Density functional theory calculations reveal a dynamical instability of the Pnma structure of Y_3Co. In particular, a transversal acoustic phonon mode along the (00z) direction has imaginary frequencies at z<1/4. Employing inelastic neutron scattering measurements we find a strong damping of the (00z) phonon mode below a critical temperature T_t. The observed structural transformation causes the reduction of dimensionality of electronic bands and decreases the electronic density of states at the Fermi level that identifies Y_3Co as a system with the charge density wave instability.
سجل دخول لتتمكن من نشر تعليقات
التعليقات
جاري جلب التعليقات
سجل دخول لتتمكن من متابعة معايير البحث التي قمت باختيارها