Physical Property Characterization of Bulk MgB2 Superconductor

139   0   0.0 ( 0 )
 نشر من قبل Veer Awana Dr
 تاريخ النشر 2012
  مجال البحث فيزياء
والبحث باللغة English




اسأل ChatGPT حول البحث

We report synthesis, structure/micro-structure, resistivity under magnetic field [R(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity K(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples of MgB2, processed under identical conditions. The compound crystallizes in hexagonal structure with space group P6/mmm. Transmission electron microscopy (TEM) reveals electron micrographs showing various types of defect features along with the presence of 3-4nm thick amorphous layers forming the grain boundaries of otherwise crystalline MgB2. Raman spectra of the compound at room temperature exhibited characteristic phonon peak at 600 cm-1. Superconductivity is observed at 37.2K by magnetic susceptibility C(T), resistivity R(T), thermoelectric power S(T), and thermal conductivity K(T) measurements. The power law fitting of R(T) give rise to Debye temperature at 1400K which is found consistent with the theoretical fitting of S(T), exhibiting ThetaD of 1410K and carrier density of 3.81x 1028/m3. Thermal conductivity K(T) shows a jump at 38K, i.e., at Tc, which was missing in some earlier reports. Critical current density (Jc) of up to 105 A/cm2 in 1-2T (Tesla) fields at temperatures (T) of up to 10K is seen from magnetization measurements. The irreversibility field, defined as the field related to merging of M(H) loops is found to be 78, 68 and 42 kOe at 4, 10 and 20K respectively. The superconducting performance parameters viz. irreversibility field (Hirr) and critical current density Jc(H) of the studied MgB2 are improved profoundly with addition of nano-SiC and nano-Diamond. The physical property parameters measured for polycrystalline MgB2 are compared with earlier reports and a consolidated insight of various physical properties is presented.



قيم البحث

اقرأ أيضاً

We report an easy single step synthesis route of title compound NdFeAsO0.80F0.20 superconductor having bulk superconductivity below 50 K. The title compound is synthesized via solid-state reaction route by encapsulation in an evacuated (10-3 Torr) qu artz tube. Rietveld analysis of powder X-ray diffraction data shows that compound crystallized in tetragonal structure with space group P4/nmm. R(T)H measurements showed superconductivity with Tc (R=0) at 48 K and a very high upper critical field (Hc2) of up to 345 Tesla. Magnetic measurements exhibited bulk superconductivity in terms of diamagnetic onset below 50 K. The lower critical field (Hc1) is around 1000 Oe at 5 K. In normal state i.e., above 60 K, the compound exhibited purely paramagnetic behavior and thus ruling out the presence of any ordered FeOx impurity in the matrix. In specific heat measurements a jump is observed in the vicinity of superconducting transition (Tc) along with an upturn at below T=4 K due to the AFM ordering of Nd+3 ions in the system. The Thermo-electric power (TEP) is negative down to Tc, thus indicating dominant carriers to be of n-type in NdFeAsO0.80F0.20 superconductor. The granularity of the bulk superconducting NdFeAsO0.8F0.2 sample is investigated and the intra and inter grain contributions have been individuated by looking at various amplitude and frequencies of the applied AC drive magnetic field.
We report the experimental and theoretical study on magnetic nature of Bi3Ni system. The structure is found to be orthorhombic (Pnma) with lattice parameters a = 8.879{AA} b = 4.0998{AA} and c = 4.099{AA}. The title compound is synthesized via a soli d state reaction route by quartz vacuum encapsulation of 5N purity stoichiometric ingredients of Ni and Bi. The superconducting transition temperature is found to be 4.1 K as confirmed from magnetization and specific heat measurements. The lower critical field (Hc1) and irreversibility field (Hirr) are around 150 and 3000Oe respectively at 2K. Upper critical field (Hc2) as determined from in field (up to 4 Tesla) ac susceptibility is found to be around 2 Tesla at 2K. The normal state specific heat is fitted using Sommerfeld-Debye equation C(T) = {gamma}T + {beta}T3+{delta}T5 and the parameters obtained are {gamma}= 11.08mJ/mol-K2, {beta}= 3.73mJ/mol-K4 and {delta}= 0.0140mJ/mol-K6. The calculated electronic density of states (DOS) at Fermi level N(EF) and Debye temperature {Theta}D are 4.697 states/eV per formula unit and 127.7K respectively. We also estimated the value of electron phonon coupling constant ({lambda}) to be 1.23, which when substituted in MacMillan equation gives Tc = 4.5K. Density functional (DFT) based calculations for experimentally determined lattice parameters show that Ni in this compound is non-magnetic and ferromagnetic interactions seem to play no role. The Stoner condition I*N(EF) = 0.136 per Ni atom also indicates that system cannot have any ferromagnetism. The fixed spin moment (FSM) calculations by fixing total magnetic moment on the unit cell also suggested that this system does not exhibit any signatures of ferromagnetism.
Superconductors with persistent zero-resistance currents serve as permanent magnets for high-field applications requiring a strong and stable magnetic field, such as magnetic resonance imaging (MRI). The recent global helium shortage has quickened re search into high-temperature superconductors (HTSs) materials that can be used without conventional liquid-helium cooling to 4.2 K. Herein, we demonstrate that 40-K-class metallic HTS magnesium diboride (MgB2) makes an excellent permanent bulk magnet, maintaining 3 T at 20 K for 1 week with an extremely high stability (<0.1 ppm/h). The magnetic field trapped in this magnet is uniformly distributed, as for single-crystalline neodymium-iron-boron. Magnetic hysteresis loop of the MgB2 permanent bulk magnet was detrmined. Because MgB2 is a simple-binary-line compound that does not contain rare-earth metals, polycrystalline bulk material can be industrially fabricated at low cost and with high yield to serve as strong magnets that are compatible with conventional compact cryocoolers, making MgB2 bulks promising for the next generation of Tesla-class permanent-magnet applications.
We report synthesis, structure, electrical transport and heat capacity of SmFeAsO. The title compound is synthesized by one-step encapsulation of stoichiometric FeAs, Sm, and Sm2O3 in an evacuated (10-5 Torr) quartz tube by prolong (72 hours) anneali ng at 1100oC. The as synthesized compound is crystallized in tetragonal structure with P4/nmm space group having lattice parameters a = 3.93726(33) A and c = 8.49802(07) A. The resistance (R-T) measurements on the compound exhibited ground state spin-density-wave (SDW)-like metallic steps below 140 K. Heat capacity CP(T) measurements on the title compound, showed an anomaly at around 140 K, which is reminiscent of the SDW ordering of the compound. At lower temperatures the CP(T) shows a clear peak at around 4.5 K. At lower temperature below 20 K, Cp(T) is also measured under an applied field of 7 Tesla. It is concluded that the CP(T) peak at 4.5 K is due to the anti-ferromagnetic(AFM) ordering of Sm3+ spins. These results are in confirmation with ordering of Sm in Sm2-xCexCuO4.
We report the effect of adipic acid (C6H10O4) doping on lattice parameters, microstructure, critical temperature (Tc), current density (Jc), and irreversibility field (Hirr) for MgB2 superconductor. Actual carbon (C) substitution level for boron (B) is estimated to be from 0.40 percent to 2.95 percent for different doping levels. A reduction in Tc from 38.43 to 34.93 K and in lattice parameter a from 3.084(3) A to 3.075(6) Ais observed for the10 wt percent C6H10O4 doped sample in comparison to pristine MgB2. This is an indication of C substitution at boron sites, with the C coming from the decomposition of C6H10O4 at the time of reaction. Interestingly the doped samples have resulted in significant enhancement of Jc and Hirr. All the doped samples exhibit the Jc value of the order of 10^4 A/cm2 at 5 K and 8 T, which is higher by an order of magnitude as compared to undoped sample. This result indicates that C6H10O4 is a promising material for MgB2 for obtaining the excellent Jc values under higher magnetic fields.