تسجيل مستخدم جديدSuperconductivity of non- stoichiometric intermetallic compound NbB2
186
0
0.0
(
0
)
اسأل ChatGPT حول البحث
ﻻ يوجد ملخص باللغة العربية
We report the synthesis, magnetic susceptibility and crystal structure analysis for NbB2+x (x = 0.0 to 1.0) samples. The study facilitates in finding a correlation among the lattice parameters, chemical composition and the superconducting transition temperature Tc. Rietveld analysis is done on the X- ray diffraction patterns of all synthesized samples to determine the lattice parameters. The a parameter decreases slightly and has a random variation with increasing x, while c parameter increases from 3.26 for pure NbB2 to 3.32 for x=0.4 i.e. NbB2.4. With higher Boron content (x>0.4) the c parameter decreases slightly. The stretching of lattice in c direction induces superconductivity in the non- stoichiometric niobium boride. Pure NbB2 is non-superconductor while the other NbB2+x (x>0.0) samples show diamagnetic signal in the temperature range 8.9-11K. Magnetization measurements (M-H) at a fixed temperature of 5K are also carried out in both increasing and decreasing directions of field. The estimated lower and upper critical fields (Hc1 & Hc2) as viewed from M-H plots are around 590 and 2000Oe respectively for NbB2.6 samples. In our case, superconductivity is achieved in NbB2 by varying the Nb/B ratios, rather than changing the processing conditions as reported by others.
قيم البحث
اقرأ أيضاً
We successfully synthesized the nickel-based compound GdONiBi with superconducting transition temperature about 4.5 K. By partially substituting the element Gd with Sr to introduce holes into the material, we got new superconductor Gd0.9Sr0.1ONiBi wi
th critical temperature about 4.7 K. The normal state resistivity in nickel-based samples shows a metallic behavior. The magnetoresistance measurements show a different behavior compared to those in iron-based compounds which indicates that the mechanism in the two kinds of superconductors maybe different.
Layered van der Waals (vdW) materials are emerging as one of the most versatile directions in the field of quantum condensed matter physics. They allow an unprecedented control of electronic properties via stacking of different types of two-dimension
al (2D) materials. A fascinating frontier, largely unexplored, is the stacking of strongly-correlated phases of matter in vdW materials. Here, we study 4Hb-TaS$_2$, which naturally realizes an alternating stacking of a Mott insulator, recently reported as a gapless spin-liquid candidate(1T-TaS$_2$), and a 2D superconductor (1H-TaS$_2$). This raises the question of how these two components affect each other. We find a superconducting ground state with a transition temperature of 2.7K, which is significantly elevated compared to the 2H polytype (Tc=0.7K). Strikingly, the superconducting state exhibits signatures of time-reversal-symmetry breaking abruptly appearing at the superconducting transition, which can be naturally explained by a chiral superconducting state.
The pressure effects on the antiferromagentic orders in iron-based ladder compounds CsFe$_2$Se$_3$ and BaFe$_2$S$_3$ have been studied using neutron diffraction. With identical crystal structure and similar magnetic structures, the two compounds exhi
bit highly contrasting magnetic behaviors under moderate external pressures. In CsFe$_2$Se$_3$ the ladders are brought much closer to each other by pressure, but the stripe-type magnetic order shows no observable change. In contrast, the stripe order in BaFe$_2$S$_3$, undergoes a quantum phase transition where an abrupt increase of N$acute{e}$el temperature by more than 50$%$ occurs at about 1 GPa, accompanied by a jump in the ordered moment. With its spin structure unchanged, BaFe$_2$S$_3$ enters an enhanced magnetic phase that bears the characteristics of an orbital selective Mott phase, which is the true neighbor of superconductivity emerging at higher pressures.
In this paper, a comprehensive study of the effects of Ni-doping on structural, electrical, thermal and magnetic properties of the NbB2 is presented. Low amounts (leq 10 %) of Ni substitution on Nb sites cause structural distortions and induce drasti
c changes in the physical properties, such as the emergence of a bulk superconducting state with anomalous behaviors in the critical fields (lower and upper) and in the specific heat. Ni-doping at the 9 at.% level, for instance, is able to increase the critical temperature (TC) in stoichiometric NbB2 (< 1.3 K) to approximately 6.0 K. Bulk superconductivity is confirmed by magnetization, electronic transport, and specific heat measurements. Both Hc1 and Hc2 critical fields exhibit a linear dependence with reduced temperature (T/TC), and the specific heat deviates remarkably from the conventional exponential temperature dependence of the single-band BCS theory. These findings suggest multiband superconductivity in the composition range from 0.01 leq x leq 0.10.
The tetragonal Mo$_5$PB$_2$ compound was recently reported to show superconductivity with a critical temperature up to 9.2 K. In search of evidence for multiple superconducting gaps in Mo$_5$PB$_2$, comprehensive measurements, including magnetic susc
eptibility, electrical resistivity, heat capacity, and muon-spin rotation and relaxation ($mu$SR) measurements were carried out. Data from both low-temperature superfluid density and electronic specific heat suggest a nodeless superconducting ground state in Mo$_5$PB$_2$. Two superconducting energy gaps $Delta_0$ = 1.02 meV (25%) and 1.49 meV (75%) are required to describe the low-$T$ electronic specific-heat data. The multigap features are clearly evidenced by the field dependence of the electronic specific-heat coefficient and the Gaussian relaxation rate in the superconducting state (i.e., superfluid density), as well as by the temperature dependence of the upper critical field. By combining our extensive experimental results with numerical band-structure calculations, we provide compelling evidence of multigap superconductivity in Mo$_5$PB$_2$.