Graphene oxide membranes show exceptional molecular permeation properties, with a promise for many applications. However, their use in ion sieving and desalination technologies is limited by a permeation cutoff of ~9 Angstrom, which is larger than hydrated ion diameters for common salts. The cutoff is determined by the interlayer spacing d ~13.5 Angstrom, typical for graphene oxide laminates that swell in water. Achieving smaller d for the laminates immersed in water has proved to be a challenge.Here we describe how to control d by physical confinement and achieve accurate and tuneable ion sieving. Membranes with d from ~ 9.8 Angstrom to 6.4 Angstrom are demonstrated, providing the sieve size smaller than typical ions hydrated diameters.In this regime, ion permeation is found to be thermally activated with energy barriers of ~10-100 kJ/mol depending on d. Importantly, permeation rates decrease exponentially with decreasing the sieve size but water transport is weakly affected (by a factor of <2). The latter is attributed to a low barrier for water molecules entry and large slip lengths inside graphene capillaries. Building on these findings, we demonstrate a simple scalable method to obtain graphene-based membranes with limited swelling, which exhibit 97% rejection for NaCl.
Download