Domain walls in ferroelectrics exhibit a plethora of phases and functionalities not found in the bulk. The interplay of electrostatic, chemical, topological, and distortive inhomogeneities at the walls can be so complex, however, that this obstructs their technological performance. In tetragonal ferroelectrics like PbZrxTi1-xO3, for example, the desired functional 180{deg} domain walls within out-of-plane-polarized c-domains are interspersed by in-plane-polarized a-domains and the associated network of domain walls remains challenging to analyze. Here we use a combination of STEM and optical second harmonic generation (SHG) to determine the relation between strain, film thickness, local electric fields and the resulting domain and domain-wall structures across the entire thickness of a set of PZT films. We quantify the distribution of a-domains in the c-domain matrix of the films. Using locally applied electric fields we control the a/c distribution and induce the technologically preferable 180{deg} domain walls. We find that these voltage induced walls are tilted and exhibit a mixed Ising-Neel type transverse rotation of polarization across the wall with a specific nonlinear optical response.
rate research
Read More
The static configuration of ferroelectric domain walls was investigated using atomic force microscopy on epitaxial PbZr0.2Ti0.8O3 thin films. Measurements of domain wall roughness reveal a power law growth of the correlation function of relative displacements B(L) ~ L^(2zeta) with zeta ~ 0.26 at short length scales L, followed by an apparent saturation at large L. In the same films, the dynamic exponent mu was found to be ~ 0.6 from independent measurements of domain wall creep. These results give an effective domain wall dimensionality of d=2.5, in good agreement with theoretical calculations for a two-dimensional elastic interface in the presence of random-bond disorder and long range dipolar interactions.
Although enhanced conductivity at ferroelectric domain boundaries has been found in BiFeO$_3$ films, Pb(Zr,Ti)O$_3$ films, and hexagonal rare-earth manganite single crystals, the mechanism of the domain wall conductivity is still under debate. Using conductive atomic force microscopy, we observe enhanced conductance at the electrically-neutral domain walls in semiconducting hexagonal ferroelectric TbMnO$_3$ thin films where the structure and polarization direction are strongly constrained along the c-axis. This result indicates that domain wall conductivity in ferroelectric rare-earth manganites is not limited to charged domain walls. We show that the observed conductivity in the TbMnO$_3$ films is governed by a single conduction mechanism, namely, the back-to-back Schottky diodes model tuned by the segregation of defects.
Ferroelectric switching and nanoscale domain dynamics were investigated using atomic force microscopy on monocrystalline Pb(Zr0.2Ti0.8)O3 thin films. Measurements of domain size versus writing time reveal a two-step domain growth mechanism, in which initial nucleation is followed by radial domain wall motion perpendicular to the polarization direction. The electric field dependence of the domain wall velocity demonstrates that domain wall motion in ferroelectric thin films is a creep process, with the critical exponent mu close to 1. The dimensionality of the films suggests that disorder is at the origin of the observed creep behavior.
Atomic force microscopy was used to investigate ferroelectric switching and nanoscale domain dynamics in epitaxial PbZr0.2Ti0.8O3 thin films. Measurements of the writing time dependence of domain size reveal a two-step process in which nucleation is followed by radial domain growth. During this growth, the domain wall velocity exhibits a v ~ exp[-(1/E)^mu] dependence on the electric field, characteristic of a creep process. The domain wall motion was analyzed both in the context of stochastic nucleation in a periodic potential as well as the canonical creep motion of an elastic manifold in a disorder potential. The dimensionality of the films suggests that disorder is at the origin of the observed domain wall creep. To investigate the effects of changing the disorder in the films, defects were introduced during crystal growth (a-axis inclusions) or by heavy ion irradiation, producing films with planar and columnar defects, respectively. The presence of these defects was found to significantly decrease the creep exponent mu, from 0.62 - 0.69 to 0.38 - 0.5 in the irradiated films and 0.19 - 0.31 in the films containing a-axis inclusions.
Mechanical restoring forces acting on ferroelastic domain walls displaced from the equilibrium positions in epitaxial films are calculated for various modes of their cooperative translational oscillations. For vibrations of the domain-wall superlattice with the wave vectors corresponding to the center and boundaries of the first Brillouin zone, the soft modes are singled out that are distinguished by a minimum magnitude of the restoring force. It is shown that, in polydomain ferroelectric thin films, the soft modes of wall vibrations may create enormously large contribution to the film permittivity.