Mixing of atoms at the interface was studied for Mn/Fe magnetic hetero-epitaxial layers on Cu(001) by scanning tunneling microscopy/spectroscopy. The formation of a surface alloy was observed when the Mn layer was thinner than 3 atomic layers. From the fourth layer, Fe segregation is suppressed, and a pure Mn surface appears. Accordingly, spectroscopic measurements revealed the electronic difference between the surface alloy and Mn layers. The surface electronic structure of the fourth Mn layer is slightly different from that of the fifth layers, which is attributed to the hybridization of the fourth layer with the underneath Fe-Mn alloy.