Monolayers of Transition Metal Dichalcogenides (TMDs) are atomically thin two-dimensional crystals with attractive optoelectronic properties, which are promising for emerging applications in nanophotonics. Here, we report on the extraordinary spatial non-uniformity of the photoluminescence (PL) and strain properties of WS2 monolayers exfoliated from the natural crystal. Specifically, it is shown that the edges of such monolayers exhibit remarkably enhanced PL intensity compared to their respective central area. A comprehensive analysis of the recombination channels involved in the PL process demonstrates a spatial non-uniformity across the monolayers surface and reflects on the non-uniformity of the intrinsic electron density across the monolayer. Auger electron imaging and spectroscopy studies complemented with PL measurements in different environments indicate that oxygen chemisorption and physisorption are the two fundamental mechanisms responsible for the observed non-uniformity. At the same time Raman spectroscopy analysis shows remarkable strain variations among the different locations of an individual monolayer, however such variations cannot be strictly correlated with the non-uniform PL emission. Our results shed light on the role of the chemical bonding on the competition between exciton complexes in monolayer WS2, providing a way of engineering new nanophotonic functions using WS2 monolayers. It is therefore envisaged that our findings could find diverse applications towards the development of TMDs-based optoelectronic devices.
rate research
Read More
The ability to efficiently evolve hydrogen via electrocatalysis at low overpotentials holds tremendous promise for clean energy. Hydrogen evolution reaction (HER) can be easily achieved from water if a voltage above the thermodynamic potential of the HER is applied. Large overpotentials are energetically inefficient but can be lowered with expensive platinum based catalysts. Replacement of Pt with inexpensive, earth abundant electrocatalysts would be significantly beneficial for clean and efficient hydrogen evolution. Towards this end, promising HER characteristics have been reported using 2H (trigonal prismatic) XS2 (where X = Mo or W) nanoparticles with a high concentration of metallic edges as electrocatalysts. The key challenges for HER with XS2 are increasing the number and catalytic activity of active sites. Here we report atomically thin nanosheets of chemically exfoliated WS2 as efficient catalysts for hydrogen evolution with very low overpotentials. Atomic-resolution transmission electron microscopy and spectroscopy analyses indicate that enhanced electrocatalytic activity of WS2 is associated with high concentration of strained metallic 1T (octahedral) phase in the as-exfoliated nanosheets. Density functional theory calculations reveal that the presence of strain in the 1T phase leads to an enhancement of the density of states at the Fermi level and increases the catalytic activity of the WS2 nanosheet. Our results suggest that chemically exfoliated WS2 nanosheets could be interesting catalysts for hydrogen evolution.
Single layers of WS2 are direct gap semiconductors with high photoluminescence (PL) yield holding great promise for emerging applications in optoelectronics. The spatial confinement in a 2D monolayer together with the weak dielectric screening lead to huge binding energies for the neutral excitons as well as other excitonic complexes, such as trions and biexcitons whose binding energies scale accordingly. Here, we report on the existence of biexcitons in mechanically exfoliated WS2 flakes from 78 K up to room temperature. Performing temperature and power dependent PL measurements, we identify the biexciton emission channel through the superlinear behavior of the integrated PL intensity as a function of the excitation power density. On the contrary, neutral and charged excitons show a linear to sublinear dependence in the whole temperature range. From the energy difference between the emission channels of the biexciton and neutral exciton, a biexciton binding energy of 65-70 meV is determined.
Transition metal dichalcogenides hold promise for applications in novel optoelectronic devices. There is therefore a need for materials that can be obtained in large quantities and with well understood optical properties. In this report, we present a thorough photoluminescence (PL) investigations of monolayer tungsten disulphide obtained via liquid phase exfoliation. As shown by microscopy studies, the exfoliated nanosheets have dimensions of tens of nanometers and thickness of 2.5 monolayers on average. The monolayer content is about 20%. Our studies show that at low temperature the photoluminescence is dominated by excitons localized on nanosheet edges. As a consequence, the PL is strongly sensitive to environment and exhibits an enhanced splitting in magnetic field. As the temperature is increased, the excitons are thermally excited out of the defect states and the dominant transition is that of the negatively charged exciton. Furthermore, upon excitation with a circularly polarized light, the PL retains a degree of polarization reaching 50% and inherited from the valley polarized photoexcited excitons. The studies of PL dynamics reveal that the PL lifetime is on the order of 10 ps, probably limited by non-radiative processes. Our results underline the potential of liquid exfoliated TMD monolayers in large scale optoelectronic devices.
Engineering atomic-scale defects is crucial for realizing wafer-scale, single-crystalline transition metal dichalcogenide monolayers for electronic devices. However, connecting atomic-scale defects to larger morphologies poses a significant challenge. Using electron microscopy and atomistic simulations, we provide insights into WS2 crystal growth mechanisms, providing a direct link between synthetic conditions and the microstructure. Dark-field TEM imaging of coalesced monolayer WS2 films illuminates defect arrays that atomic-resolution STEM imaging identifies as translational grain boundaries. Imaging reveals the films to have nearly a single orientation with imperfectly stitched domains. Through atomic-resolution imaging and ReaxFF reactive force field-based molecular dynamics simulations, we observe two types of translational mismatch and discuss their atomic structures and origin. Our results indicate that the mismatch results from relatively fast growth rates. Through statistical analysis of >1300 facets, we demonstrate that the macrostructural features are constructed from nanometer-scale building blocks, describing the system across sub-{AA}ngstrom to multi-micrometer length scales.
We measured the chemical and magnetic depth profiles of a single crystalline (La$_{1-x}$Pr$_x$)$_{1-y}$Ca$_y$MnO$_{3-{delta}}$ (x = 0.52pm0.05, y = 0.23pm0.04, {delta} = 0.14pm0.10) film grown on a NdGaO3 substrate using x-ray reflectometry, electron microscopy, electron energy-loss spectroscopy and polarized neutron reflectometry. Our data indicate that the film exhibits coexistence of different magnetic phases as a function of depth. The magnetic depth profile is correlated with a variation of chemical composition with depth. The thermal hysteresis of ferromagnetic order in the film suggests a first order ferromagnetic transition at low temperatures.