Irradiation effects in Ni-17Mo-7Cr alloy, which is an newly developed structural material for molten salt reactor (MSR), have been systematically investigated by using 3MeV Au ions at different fluences, corresponding to dpa number (displacement per atom) of 1~ 30. GIXRD measurement indicates that the microstrain of the irradiated samples increased from 0.14% to 0.22% as dpa increased from 1 to 30. In the meanwhile, nanoindentation results reveal the Ni-17Mo-7Cr alloy underwent radiation-induced hardening first and then softening at dpa of 30. The swelling rate of Ni-17Mo-7Cr alloy was found around 1.3% at 30 dpa, which means only 0.04% per dpa. Besides, Raman spectra shows that carbon segregation appeared after Au ions irradiation. Our results are very helpful for understanding irradiation damages in Nickel-base alloys, especially for those in purpose of being used in future MSR nuclear energy system.