The magnetic domain structure and magnetic properties of a ferromagnetic (Ga,Mn)As epilayer with perpendicular magnetic easy-axis are investigated. We show that, despite strong hysteresis, domain theory at thermodynamical equilibrium can be used to determine the micromagnetic parameters. Combining magneto-optical Kerr microscopy, magnetometry and ferromagnetic resonance measurements, we obtain the characteristic parameter for magnetic domains $lambda_c$, the domain wall width and specific energy, and the spin stiffness constant as a function of temperature. The nucleation barrier for magnetization reversal and the Walker breakdown velocity for field-driven domain wall propagation are also estimated.
rate research
Read More
(Ga,Mn)As is at the forefront of research exploring the synergy of magnetism with the physics and technology of semiconductors, and has led to discoveries of new spin-dependent phenomena and functionalities applicable to a wide range of material systems. Its recognition and utility as an ideal model material for spintronics research has been undermined by the large scatter in reported semiconducting doping trends and micromagnetic parameters. In this paper we establish these basic material characteristics by individually optimizing the highly non-equilibrium synthesis for each Mn-doping level and by simultaneously determining all micromagnetic parameters from one set of magneto-optical pump-and-probe measurements. Our (Ga,Mn)As thin-film epilayers, spannig the wide range of accessible dopings, have sharp thermodynamic Curie point singularities typical of uniform magnetic systems. The materials show systematic trends of increasing magnetization, carrier density, and Curie temperature (reaching 188 K) with increasing doping, and monotonous doping dependence of the Gilbert damping constant of ~0.1-0.01 and the spin stiffness of ~2-3 meVnm^2. These results render (Ga,Mn)As well controlled degenerate semiconductor with basic magnetic characteristics comparable to common band ferromagnets.
We report on the determination of micromagnetic parameters of epilayers of the ferromagnetic semiconductor (Ga,Mn)As, which has easy axis in the sample plane, and (Ga,Mn)(As,P) which has easy axis perpendicular to the sample plane. We use an optical analog of ferromagnetic resonance where the laser-pulse-induced precession of magnetization is measured directly in the time domain. By the analysis of a single set of pump-and-probe magneto-optical data we determined the magnetic anisotropy fields, the spin stiffness and the Gilbert damping constant in these two materials. We show that incorporation of 10% of phosphorus in (Ga,Mn)As with 6% of manganese leads not only to the expected sign change of the perpendicular to plane anisotropy field but also to an increase of the Gilbert damping and to a reduction of the spin stiffness. The observed changes in the micromagnetic parameters upon incorporating P in (Ga,Mn)As are consistent with the reduced hole density, conductivity, and Curie temperature of the (Ga,Mn)(As,P) material. We report that the magnetization precession damping is stronger for the n = 1 spin wave resonance mode than for the n = 0 uniform magnetization precession mode.
We demonstrate that the interplay of in-plane biaxial and uniaxial anisotropy fields in (Ga,Mn)As results in a magnetization reorientation transition and an anisotropic AC susceptibility which is fully consistent with a simple single domain model. The uniaxial and biaxial anisotropy constants vary respectively as the square and fourth power of the spontaneous magnetization across the whole temperature range up to T_C. The weakening of the anisotropy at the transition may be of technological importance for applications involving thermally-assisted magnetization switching.
We have investigated the domain wall resistance for two types of domain walls in a (Ga,Mn)As Hall bar with perpendicular magnetization. A sizeable positive intrinsic DWR is inferred for domain walls that are pinned at an etching step, which is quite consistent with earlier observations. However, much lower intrinsic domain wall resistance is obtained when domain walls are formed by pinning lines in unetched material. This indicates that the spin transport across a domain wall is strongly influenced by the nature of the pinning.
We have studied current-driven domain wall motion in modified Ga_0.95Mn_0.05As Hall bar structures with perpendicular anisotropy by using spatially resolved Polar Magneto-Optical Kerr Effect Microscopy and micromagnetic simulation. Regardless of the initial magnetic configuration, the domain wall propagates in the opposite direction to the current with critical current of 1~2x10^5A/cm^2. Considering the spin transfer torque term as well as various effective magnetic field terms, the micromagnetic simulation results are consistent with the experimental results. Our simulated and experimental results suggest that the spin-torque rather than Oersted field is the reason for current driven domain wall motion in this material.